LNP™ LUBRICOMP™ Compound KP004 - Americas

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP* KP004 is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Coefficient of friction

0.14 - 0.25 [-]

Show Supplier Material materials with Coefficient of friction of 0.14 - 0.25 [-]

Coefficient of friction, kinetic

0.25 [-]

Show Supplier Material materials with Coefficient of friction, kinetic of 0.25 [-]

ASTM D 3702 Modified: Manual

Coefficient of friction, static

0.14 [-]

Show Supplier Material materials with Coefficient of friction, static of 0.14 [-]

ASTM D 3702 Modified: Manual

Density

23.0 °C

1.48 g/cm³

Show Supplier Material materials with Density of 1.48 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

21.5 %

Show Supplier Material materials with Elongation of 21.5 %

ISO 527 | yield, 5 mm/min

Flexural modulus

23.0 °C

1.8 GPa

Show Supplier Material materials with Flexural modulus of 1.8 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

60 MPa

Show Supplier Material materials with Flexural strength of 60 MPa

ISO 178

Impact strength, Izod notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A | 80*10*4, 23°C

Impact strength, Izod unnotched

23.0 °C

35 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 35 kJ/m²

ISO 180/1U | unnotched 80*10*4, 23°C

Tensile strength

23.0 °C

39 MPa

Show Supplier Material materials with Tensile strength of 39 MPa

ISO 527 | break, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.11E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.11E-4 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature

79 °C

Show Supplier Material materials with Heat deflection temperature of 79 °C

Heat deflection temperature, 1.80 MPa

79 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 79 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Rheological Properties

PropertyTemperatureValueComment

Shrinkage, transverse

23.0 °C

2.1 %

Show Supplier Material materials with Shrinkage, transverse of 2.1 %

ASTM D 955 | 24 hrs

Technological properties

Property
Application areas

Seating/Chair, ATM/Ticket Machine

Availability

Europe,Americas

Processing methods

Melt Temperature: 200 to 215.0°C
Middle - Zone 2 Temperature: 195 to 205.0°C
Screw Speed: 30 to 60.0rpm
Back Pressure: 0.2 to 0.3MPa
Drying Temperature: 80°C
Front - Zone 3 Temperature: 210 to 220.0°C
Rear - Zone 1 Temperature: 175 to 190.0°C
Drying Time: 4hrs
Mold Temperature: 80 to 110.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.