LNP™ LUBRICOMP™ Compound KP004 - Europe

Want to keep this datasheet? Save it now in your required format

Description

LNP LUBRICOMP* KP004 is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Consumer Goods

Decorative Applications

General Appliances

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Coefficient of friction		0.14 - 0.25 [-] Show Supplier Material materials with Coefficient of friction of 0.14 - 0.25 [-]
Coefficient of friction, kinetic		0.25 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.25 [-]	ASTM D 3702 Modified: Manual
Coefficient of friction, static		0.14 [-] Show Supplier Material materials with Coefficient of friction, static of 0.14 [-]	ASTM D 3702 Modified: Manual
Density	23.0 °C	1.48 g/cm³ Show Supplier Material materials with Density of 1.48 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	15 % Show Supplier Material materials with Elongation of 15 %	>, ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	1.8 GPa Show Supplier Material materials with Flexural modulus of 1.8 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	47 MPa Show Supplier Material materials with Flexural strength of 47 MPa	ISO 178 \| break, 2 mm/min
Impact strength, Izod notched	23.0 °C	5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²	ISO 180/1A \| 80104, 23°C
Impact strength, Izod unnotched	23.0 °C	35 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 35 kJ/m²	ISO 180/1U \| unnotched 80104, 23°C
Tensile strength	23.0 °C	39 MPa Show Supplier Material materials with Tensile strength of 39 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1.1E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.1E-4 1/K	ISO 11359-2 \| 23°C to 60°C
Heat deflection temperature		79 °C Show Supplier Material materials with Heat deflection temperature of 79 °C
Heat deflection temperature, 1.80 MPa		79 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 79 °C	ISO 75/Af \| Flatw 80104 sp=64mm

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage, transverse	23.0 °C	2.1 % Show Supplier Material materials with Shrinkage, transverse of 2.1 %	ISO 294 \| 24 hrs

Technological properties

Property
Application areas	Seating/Chair, ATM/Ticket Machine
Availability	Europe,Americas
Processing methods	Drying Temperature: 80°C Mold Temperature: 80 to 110.0°C Screw Speed: 30 to 60.0rpm Melt Temperature: 200 to 215.0°C Rear - Zone 1 Temperature: 175 to 190.0°C Middle - Zone 2 Temperature: 195 to 205.0°C Back Pressure: 0.2 to 0.3MPa Drying Time: 4hrs Front - Zone 3 Temperature: 210 to 220.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.