ULTEM™ Resin AUT195 - Americas

Want to keep this datasheet? Save it now in your required format

Description

High flow Polyetherimide blend for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 195C (SABIC test method).

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.27 g/cm³

Show Supplier Material materials with Density of 1.27 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.5 %

Show Supplier Material materials with Moisture absorption of 0.5 %

ISO 62 | (23°C / 50% RH)

Water absorption

23.0 °C

0.9 %

Show Supplier Material materials with Water absorption of 0.9 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3 GPa

Show Supplier Material materials with Elastic modulus of 3 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

70 %

Show Supplier Material materials with Elongation of 70 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

3.1 GPa

Show Supplier Material materials with Flexural modulus of 3.1 GPa

ISO 178 | 2 mm/min

Impact strength, Charpy notched

23.0 °C

4 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, -30°C

Impact strength, Izod notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A | 80*10*4, -30°C

Tensile strength

23.0 °C

96 MPa

Show Supplier Material materials with Tensile strength of 96 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

6E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 6E-5 1/K

ISO 11359-2 | 23°C to 150°C

Coefficient of thermal expansion, transverse

23.0 °C

6E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6E-5 1/K

ISO 11359-2 | 23°C to 150°C

Heat deflection temperature

180 - 195 °C

Show Supplier Material materials with Heat deflection temperature of 180 - 195 °C

Heat deflection temperature, 0.45 MPa

195 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 195 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Heat deflection temperature, 1.80 MPa

180 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 180 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Thermal conductivity

23.0 °C

0.23 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.23 W/(m·K)

ISO 8302

Vicat softening temperature

205 °C

Show Supplier Material materials with Vicat softening temperature of 205 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

24 g/10min

Show Supplier Material materials with Melt mass-flow rate of 24 g/10min

ASTM D 1238 | 337°C/6.6 kgf

Melt volume-flow rate

16 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 16 cm³/10min

ISO 1133 | MVR at 340°C/5.0 kg

Shrinkage, transverse

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage, transverse of 0.5 %

SABIC method | on tensile bar

Technological properties

Property
Application areas

Forward Lighting, Trim

Availability

Europe,Americas

Processing methods

Melt Temperature: 340 to 380.0°C
Front - Zone 3 Temperature: 340 to 360.0°C
Drying Temperature: 130 to 140.0°C
Hopper Temperature: 80 to 100.0°C
Drying Time: 3 to 4.0hrs
Nozzle Temperature: 340 to 360.0°C
Middle - Zone 2 Temperature: 330 to 350.0°C
Rear - Zone 1 Temperature: 320 to 340.0°C
Mold Temperature: 125 to 140.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.