ULTEM 1010M resin is an amorphous, transparent polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217C. This inherently flame retardant resin is RoHS compliant. ULTEM 1010M resin is an unreinforced general purpose grade offering high heat resistance, high strength and modulus and broad chemical resistance up to high temperatures with enhanced flow and optimized mold release for metallized reflectors.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Limiting oxygen index

23.0 °C

44 %

Show Supplier Material materials with Limiting oxygen index of 44 %

Water absorption

23.0 °C

0.25 %

Show Supplier Material materials with Water absorption of 0.25 %

ASTM D 570 | (23°C/24hrs)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.6 GPa

Show Supplier Material materials with Elastic modulus of 3.6 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

60 %

Show Supplier Material materials with Elongation of 60 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

3.5 GPa

Show Supplier Material materials with Flexural modulus of 3.5 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

165 MPa

Show Supplier Material materials with Flexural strength of 165 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

32 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 32 kJ/m²

ASTM D 256 | notched, 23°C

Taber Abrasion

23.0 °C

10 mg/1000cy

Show Supplier Material materials with Taber Abrasion of 10 mg/1000cy

ASTM D 1044 | CS-17, 1 kg

Tensile strength

23.0 °C

110 MPa

Show Supplier Material materials with Tensile strength of 110 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5.58E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 5.58E-5 1/K

ASTM E 831 | -20°C to 150°C

Heat deflection temperature

198 - 207 °C

Show Supplier Material materials with Heat deflection temperature of 198 - 207 °C

Heat deflection temperature, 0.45 MPa

207 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 207 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

198 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 198 °C

ASTM D 648 | 6.4 mm, unannealed

Thermal conductivity

23.0 °C

0.22 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.22 W/(m·K)

ASTM C177

Vicat softening temperature

218 °C

Show Supplier Material materials with Vicat softening temperature of 218 °C

ASTM D 1525 | Rate B/50

Flammability

NBS Smoke Density, Flaming, Ds 4 min: 2- ASTM E 662

Electrical

PropertyTemperatureValueComment

Dielectric strength

23.0 °C

32.6 kV/mm

Show Supplier Material materials with Dielectric strength of 32.6 kV/mm

ASTM D 149 | in air, 1.6 mm

Dissipation factor

23.0 °C

2.5E-3 [-]

Show Supplier Material materials with Dissipation factor of 2.5E-3 [-]

ASTM D 150 | 2450 MHz

Volume resistivity

23.0 °C

1.00E+17 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Motorcycle, Pharmaceutical Manufacturing, Circuit Protection, Heavy Vehicles

Availability

Europe,Asia,Americas

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.