ULTEM™ Resin HU1000E - Asia

Want to keep this datasheet? Save it now in your required format

Description

Transparent, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI); food contact compliant; Steam, Gamma, EtO, and E-beam sterilizable.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.27 g/cm³

Show Supplier Material materials with Density of 1.27 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.7 %

Show Supplier Material materials with Moisture absorption of 0.7 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.27 [-]

Show Supplier Material materials with Relative density of 1.27 [-]

ASTM D 792 |

Water absorption

23.0 °C

1.25 %

Show Supplier Material materials with Water absorption of 1.25 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.2 GPa

Show Supplier Material materials with Elastic modulus of 3.2 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

6 %

Show Supplier Material materials with Elongation of 6 %

ISO 527 | yield, 5 mm/min

Flexural modulus

23.0 °C

3.3 GPa

Show Supplier Material materials with Flexural modulus of 3.3 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

160 MPa

Show Supplier Material materials with Flexural strength of 160 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

4 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m²

ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C

Impact strength, Izod notched

23.0 °C

6 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m²

ISO 180/1A | 80*10*4, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

53 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 53 J/m

ASTM D 256

Impact strength, Izod unnotched, ASTM

23.0 °C

1335 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1335 J/m

ASTM D 4812 | 23°C

Instrumented Impact, Total Energy

23.0 °C

38 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 38 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

85 MPa

Show Supplier Material materials with Tensile strength of 85 MPa

ISO 527 | break, 5 mm/min

Impact strength, Charpy unnotched

ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C

Impact strength, Izod unnotched

ISO 180/1U | unnotched 80*10*4

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 5.5E-5 1/K

ISO 11359-2 | 23°C to 150°C

Coefficient of thermal expansion, transverse

23.0 °C

5.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.5E-5 1/K

ISO 11359-2 | 23°C to 150°C

Heat deflection temperature

188 - 207 °C

Show Supplier Material materials with Heat deflection temperature of 188 - 207 °C

Heat deflection temperature, 0.45 MPa

207 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 207 °C

ASTM D 648 | 3.2 mm, unannealed

Heat deflection temperature, 1.80 MPa

188 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 188 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Vicat softening temperature

212 °C

Show Supplier Material materials with Vicat softening temperature of 212 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

12 g/10min

Show Supplier Material materials with Melt mass-flow rate of 12 g/10min

ASTM D 1238 | 337°C/6.6 kgf

Melt volume-flow rate

17 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 17 cm³/10min

ISO 1133 | MVR at 360°C/5.0 kg

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Surgical Devices, Animal Testing

Availability

Europe,Asia,Americas

Processing methods

Nozzle Temperature: 345 to 400.0°C
Shot to Cylinder Size: 40 to 60.0%
Drying Temperature: 150°C
Middle - Zone 2 Temperature: 340 to 400.0°C
Drying Time: 4 to 6.0hrs
Back Pressure: 0.3 to 0.7MPa
Mold Temperature: 135 to 165.0°C
Maximum Moisture Content: 0.02%
Rear - Zone 1 Temperature: 330 to 400.0°C
Front - Zone 3 Temperature: 345 to 400.0°C
Vent Depth: 0.025 to 0.076mm
Screw Speed: 40 to 70.0rpm
Melt Temperature: 350 to 400.0°C
Drying Time (Cumulative): 24hrs

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.