Description

Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.28 g/cm³

Show Supplier Material materials with Density of 1.28 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.2 %

Show Supplier Material materials with Moisture absorption of 0.2 %

ISO 62 | (23°C / 50% RH)

Relative density

23.0 °C

1.28 [-]

Show Supplier Material materials with Relative density of 1.28 [-]

ASTM D 792

Water absorption

23.0 °C

1.2 %

Show Supplier Material materials with Water absorption of 1.2 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.9 GPa

Show Supplier Material materials with Elastic modulus of 2.9 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

50 %

Show Supplier Material materials with Elongation of 50 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

2.9 GPa

Show Supplier Material materials with Flexural modulus of 2.9 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

110 MPa

Show Supplier Material materials with Flexural strength of 110 MPa

ISO 178 | yield, 2 mm/min

Impact strength, Charpy notched

23.0 °C

7 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m²

ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm

Impact strength, Izod notched

23.0 °C

5 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A | 80*10*4, -30°C

Impact strength, Izod notched, ASTM

23.0 °C

59 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 59 J/m

ASTM D 256

Impact strength, Izod unnotched, ASTM

23.0 °C

2100 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 2100 J/m

ASTM D 4812 | 23°C

Instrumented Impact, Total Energy

23.0 °C

30 J

Show Supplier Material materials with Instrumented Impact, Total Energy of 30 J

ASTM D 3763 | 23°C

Tensile strength

23.0 °C

85 MPa

Show Supplier Material materials with Tensile strength of 85 MPa

ISO 527 | break, 5 mm/min

Impact strength, Charpy unnotched

ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C

Impact strength, Izod unnotched

ISO 180/1U | unnotched 80*10*4

Thermal

PropertyTemperatureValueComment

Ball Pressure Test

Passes

IEC 60695-10-2 | 125°C +/- 2°C

Coefficient of thermal expansion

23.0 °C

5.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 5.5E-5 1/K

ISO 11359-2 | 23°C to 150°C

Coefficient of thermal expansion, transverse

23.0 °C

5.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.5E-5 1/K

ISO 11359-2 | 23°C to 150°C

Heat deflection temperature

198 - 208 °C

Show Supplier Material materials with Heat deflection temperature of 198 - 208 °C

Heat deflection temperature, 0.45 MPa

208 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 208 °C

ISO 75/Bf | Flatw 80*10*4 sp=64mm

Heat deflection temperature, 1.80 MPa

198 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 198 °C

ISO 75/Af | Flatw 80*10*4 sp=64mm

Thermal conductivity

23.0 °C

0.31 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.31 W/(m·K)

ASTM C177

Vicat softening temperature

220 °C

Show Supplier Material materials with Vicat softening temperature of 220 °C

ISO 306 | Rate A/50

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

150 V

Show Supplier Material materials with Comparative tracking index of 150 V

IEC 60112 |

Dielectric constant, 60Hz

23.0 °C

3.2 [-]

Show Supplier Material materials with Dielectric constant, 60Hz of 3.2 [-]

ASTM D 150 | 50/60 Hz

Dielectric strength

23.0 °C

18.1 kV/mm

Show Supplier Material materials with Dielectric strength of 18.1 kV/mm

IEC 60243-1 | in oil, 3.2 mm,

Dissipation factor, 50Hz

23.0 °C

2.1E-3 [-]

Show Supplier Material materials with Dissipation factor, 50Hz of 2.1E-3 [-]

IEC 60250 | 50/60 Hz

Sheet resistivity, ROA

23.0 °C

1.00E+15 Ω

Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω

>, IEC 60093

Volume resistivity

23.0 °C

2.50E+15 Ω·cm

Show Supplier Material materials with Volume resistivity of 2.50E+15 Ω·cm

IEC 60093

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

11 g/10min

Show Supplier Material materials with Melt mass-flow rate of 11 g/10min

ASTM D 1238 | 337°C/6.6 kgf

Melt volume-flow rate

20 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 20 cm³/10min

ISO 1133 | MVR at 360°C/5.0 kg

Shrinkage

23.0 °C

0.4 %

Show Supplier Material materials with Shrinkage of 0.4 %

SABIC method | on tensile bar

Shrinkage, transverse

23.0 °C

0.4 %

Show Supplier Material materials with Shrinkage, transverse of 0.4 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Air Cabin Interiors, Electronic Components

Availability

Europe,Asia,Americas

Processing methods

Middle - Zone 2 Temperature: 355 to 375.0°C
Drying Time: 4 to 6.0hrs
Screw Speed: 40 to 70.0rpm
Rear - Zone 1 Temperature: 345 to 365.0°C
Mold Temperature: 135 to 165.0°C
Nozzle Temperature: 360 to 380.0°C
Drying Temperature: 150°C
Maximum Moisture Content: 0.02%
Front - Zone 3 Temperature: 365 to 390.0°C
Back Pressure: 0.3 to 0.7MPa
Shot to Cylinder Size: 40 to 60.0%
Vent Depth: 0.025 to 0.076mm
Melt Temperature: 365 to 390.0°C
Drying Time (Cumulative): 24hrs

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.