ULTEM™ Resin AUT200M - Europe

Want to keep this datasheet? Save it now in your required format

Description

High flow Polyetherimide (Tg 217C) with internal mold release.. Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 204C (SABIC IP method).

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Automotive

General Automotive Parts

Automotive Exterior

Road Vehicle Systems

Car Lighting

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.27 g/cm³ Show Supplier Material materials with Density of 1.27 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.7 % Show Supplier Material materials with Moisture absorption of 0.7 %	ISO 62 \| (23°C / 50% RH)
Water absorption	23.0 °C	1.25 % Show Supplier Material materials with Water absorption of 1.25 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	3.3 GPa Show Supplier Material materials with Elastic modulus of 3.3 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	60 % Show Supplier Material materials with Elongation of 60 %	ISO 527 \| break, 50 mm/min
Flexural modulus	23.0 °C	3.3 GPa Show Supplier Material materials with Flexural modulus of 3.3 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	160 MPa Show Supplier Material materials with Flexural strength of 160 MPa	ISO 178 \| yield, 2 mm/min
Hardness, Ball Indentation	23.0 °C	140 MPa Show Supplier Material materials with Hardness, Ball Indentation of 140 MPa	ISO 2039-1 \| H358/30
Impact strength, Izod notched	23.0 °C	5 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 5 kJ/m²	ISO 180/1A \| notched 80104, -30°C
Taber Abrasion	23.0 °C	10 mg/1000cy Show Supplier Material materials with Taber Abrasion of 10 mg/1000cy	SABIC method \| CS-17, 1 kg
Tensile strength	23.0 °C	105 MPa Show Supplier Material materials with Tensile strength of 105 MPa	ISO 527 \| yield, 50 mm/min
Impact strength, Izod unnotched	ISO 180/1U \| unnotched 80104, -30°C

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 5E-5 1/K	ISO 11359-2 \| 23°C to 150°C
Coefficient of thermal expansion, transverse	23.0 °C	5E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5E-5 1/K	ISO 11359-2 \| 23°C to 150°C
Heat deflection temperature		190 - 195 °C Show Supplier Material materials with Heat deflection temperature of 190 - 195 °C
Heat deflection temperature, 0.45 MPa		195 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 195 °C	ISO 75/Be \| Edgew 120104 sp=100mm
Heat deflection temperature, 1.80 MPa		190 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 190 °C	ISO 75/Ae \| Edgew 120104 sp=100mm
Thermal conductivity	23.0 °C	0.24 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.24 W/(m·K)	ISO 8302
Vicat softening temperature		212 °C Show Supplier Material materials with Vicat softening temperature of 212 °C	ISO 306 \| Rate B/120

Rheological Properties

Property	Temperature	Value	Comment
Melt volume-flow rate		13 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 13 cm³/10min	ISO 1133 \| MVR at 340°C/5.0 kg
Shrinkage	23.0 °C	0.5 % Show Supplier Material materials with Shrinkage of 0.5 %	SABIC method \| on tensile bar

Technological properties

Property
Application areas	Forward Lighting, Lighting
Availability	Europe
Processing methods	Nozzle Temperature: 350 to 405.0°C Rear - Zone 1 Temperature: 340 to 395.0°C Melt Temperature: 370 to 410.0°C Drying Time: 4 to 6.0hrs Drying Temperature: 150°C Mold Temperature: 140 to 180.0°C Front - Zone 3 Temperature: 360 to 415.0°C Hopper Temperature: 80 to 120.0°C Maximum Moisture Content: 0.02% Middle - Zone 2 Temperature: 350 to 405.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.