ULTEM™ Resin AR9300 - Europe

Want to keep this datasheet? Save it now in your required format

Description

30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Manufacturing

Additive Manufacturing

Railway

Aerospace

Aerospace Materials

Aircraft Interiors

Defense

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	9.5 GPa Show Supplier Material materials with Elastic modulus of 9.5 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	2 % Show Supplier Material materials with Elongation of 2 %	ISO 527 \| break, 5 mm/min
Flexural modulus	23.0 °C	8.5 GPa Show Supplier Material materials with Flexural modulus of 8.5 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	225 MPa Show Supplier Material materials with Flexural strength of 225 MPa	ISO 178 \| yield, 2 mm/min
Tensile strength	23.0 °C	165 MPa Show Supplier Material materials with Tensile strength of 165 MPa	ISO 527 \| break, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	208 °C Show Supplier Material materials with Heat deflection temperature of 208 °C
Heat deflection temperature, 1.80 MPa	208 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 208 °C	ISO 75/Ae \| Edgew 120104 sp=100mm
Flammability	OSU peak heat release rate (5 minute test): 40kW/m² FAR 25.853

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.2 % Show Supplier Material materials with Shrinkage of 0.2 %	SABIC method \| on tensile bar

Technological properties

Property
Application areas	Enclosure/Housing/Cover, Air Cabin Interiors, Aircraft Seating, Aerospace
Availability	Europe,Asia,Americas
Processing methods	Drying Time: 4 to 6.0hrs Maximum Moisture Content: 0.02% Melt Temperature: 350 to 400.0°C Drying Temperature: 150°C Front - Zone 3 Temperature: 350 to 410.0°C Nozzle Temperature: 350 to 410.0°C Hopper Temperature: 80 to 120.0°C Rear - Zone 1 Temperature: 350 to 370.0°C Middle - Zone 2 Temperature: 350 to 400.0°C Mold Temperature: 135 to 140.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.