ULTEM™ Resin AR9200 - Americas

Want to keep this datasheet? Save it now in your required format

Description

20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Relative density

23.0 °C

1.4 [-]

Show Supplier Material materials with Relative density of 1.4 [-]

ASTM D 792 |

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

6.96 GPa

Show Supplier Material materials with Elastic modulus of 6.96 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

3 %

Show Supplier Material materials with Elongation of 3 %

ASTM D 638 | brk, Type I, 5 mm/min

Flexural modulus

23.0 °C

7.23 GPa

Show Supplier Material materials with Flexural modulus of 7.23 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

206 MPa

Show Supplier Material materials with Flexural strength of 206 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Impact strength, Izod notched

23.0 °C

101 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 101 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

101 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 101 J/m

ASTM D 256 | notched, 23°C

Tensile strength

23.0 °C

151 MPa

Show Supplier Material materials with Tensile strength of 151 MPa

ASTM D 638 | brk, Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

211 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 211 °C

ASTM D 648 | 6.4 mm, unannealed

Flammability

NBS Smoke Density, Flaming, Ds 4 min: 5- ASTM E 662 <br> NBS Smoke Density, Flaming, Dmax: 5- ASTM E 662 <br> OSU peak heat release rate (5 minute test): 40kW/m² FAR 25.853 <br> Vertical Burn b (12s) passes at: 0sec FAR 25.853 <br> Vertical Burn a (60s) passes at: 0sec FAR 25.853 <br> NBS Smoke Density, Flaming, Ds 1.5 min: 0- ASTM E 662 <br> FAA Flammability, FAR 25.853 A/B: NATURAL- FAR 25.853

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

5.7 g/10min

Show Supplier Material materials with Melt mass-flow rate of 5.7 g/10min

ASTM D 1238 | 337°C/6.6 kgf

Shrinkage

23.0 °C

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Aerospace, Aircraft Seating, Air Cabin Interiors, Electronic Components

Availability

Asia,Americas

Features

High Stiffness, Hydrolytic Stability, Chemical Resistance, Low Smoke and Toxicity, Good Mechanicals in Broad Temperature Range, Low Creep Sensitivity, Low Shrinkage, Good metal adhesion, Amorphous, High Strength, High Heat Resistance, Good dimensional stability, Flame Retardant

Processing methods

Mold Temperature: 135 to 165.0°C
Shot to Cylinder Size: 40 to 60.0%
Rear - Zone 1 Temperature: 345 to 365.0°C
Back Pressure: 0.3 to 0.7MPa
Maximum Moisture Content: 0.02%
Front - Zone 3 Temperature: 365 to 390.0°C
Middle - Zone 2 Temperature: 355 to 375.0°C
Drying Temperature: 150°C
Nozzle Temperature: 360 to 380.0°C
Melt Temperature: 365 to 390.0°C
Vent Depth: 0.025 to 0.076mm
Drying Time: 4 to 6.0hrs
Drying Time (Cumulative): 24hrs
Screw Speed: 40 to 70.0rpm

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.