ULTEM™ Resin AR9110 - Americas

Want to keep this datasheet? Save it now in your required format

Description

10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Manufacturing

Additive Manufacturing

Railway

Aerospace

Aerospace Materials

Aircraft Interiors

Defense

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Relative density	23.0 °C	1.4 [-] Show Supplier Material materials with Relative density of 1.4 [-]	ASTM D 792 \|

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	4.5 GPa Show Supplier Material materials with Elastic modulus of 4.5 GPa	ASTM D 638 \| 5 mm/min
Elongation	23.0 °C	8 % Show Supplier Material materials with Elongation of 8 %	ASTM D 638 \| brk, Type I, 5 mm/min
Flexural modulus	23.0 °C	4.8 GPa Show Supplier Material materials with Flexural modulus of 4.8 GPa	ASTM D 790 \| 2.6 mm/min, 100 mm span
Flexural strength	23.0 °C	188 MPa Show Supplier Material materials with Flexural strength of 188 MPa	ASTM D 790 \| yld, 2.6 mm/min, 100 mm span
Impact strength, Izod notched	23.0 °C	58 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 58 kJ/m²	ASTM D 256 \| notched, 23°C
Impact strength, Izod notched, ASTM	23.0 °C	58 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 58 J/m	ASTM D 256
Tensile strength	23.0 °C	102 MPa Show Supplier Material materials with Tensile strength of 102 MPa	ASTM D 638 \| brk, Type I, 5 mm/min

Thermal

Property	Value	Comment
Heat deflection temperature	207 °C Show Supplier Material materials with Heat deflection temperature of 207 °C
Heat deflection temperature, 1.80 MPa	207 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 207 °C	ASTM D 648 \| 6.4 mm, unannealed
Flammability	NBS Smoke Density, Flaming, Dmax: 5- ASTM E 662 <br> NBS Smoke Density, Flaming, Ds 4 min: 5- ASTM E 662 <br> OSU peak heat release rate (5 minute test): 36kW/m² FAR 25.853 <br> NBS Smoke Density, Flaming, Ds 1.5 min: 0- ASTM E 662 <br> FAA Flammability, FAR 25.853 A/B: NATURAL- FAR 25.853

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	12.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 12.5 g/10min	ASTM D 1238 \| 337°C/6.6 kgf

Technological properties

Property
Application areas	Air Cabin Interiors, Aerospace
Availability	Americas
Processing methods	Front - Zone 3 Temperature: 365 to 390.0°C Vent Depth: 0.025 to 0.076mm Drying Temperature: 150°C Drying Time (Cumulative): 24hrs Maximum Moisture Content: 0.02% Shot to Cylinder Size: 40 to 60.0% Back Pressure: 0.3 to 0.7MPa Middle - Zone 2 Temperature: 355 to 375.0°C Drying Time: 4 to 6.0hrs Mold Temperature: 135 to 165.0°C Screw Speed: 40 to 70.0rpm Nozzle Temperature: 360 to 380.0°C Melt Temperature: 365 to 390.0°C Rear - Zone 1 Temperature: 345 to 365.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.