LNP™ THERMOCOMP™ Compound AB002 - Asia

Want to keep this datasheet? Save it now in your required format

Description

LNP THERMOCOMP AB002 is a compound based on ABS resin containing 10% Glass Bead.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.12 g/cm³

Show Supplier Material materials with Density of 1.12 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.65 GPa

Show Supplier Material materials with Elastic modulus of 2.65 GPa

ASTM D 638 | 50 mm/min

Elongation

23.0 °C

3.1 %

Show Supplier Material materials with Elongation of 3.1 %

ASTM D 638 | break

Impact strength, Izod notched

23.0 °C

120 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 120 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

120 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 120 J/m

ASTM D 256 | notched, 23°C

Impact strength, Izod unnotched, ASTM

23.0 °C

600 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 600 J/m

ASTM D 4812 | 23°C

Tensile strength

23.0 °C

34 MPa

Show Supplier Material materials with Tensile strength of 34 MPa

ASTM D 638 | break

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.7 %

Show Supplier Material materials with Shrinkage of 0.7 %

ASTM D 955 | 24 hrs

Technological properties

Property
Availability

Asia,Americas

Features

Good dimensional stability, Low Warpage, Structural

Processing methods

Maximum Moisture Content: 0.05 to 0.1%
Screw Speed: 30 to 60.0rpm
Middle - Zone 2 Temperature: 230 to 245.0°C
Back Pressure: 0.2 to 0.3MPa
Front - Zone 3 Temperature: 265 to 275.0°C
Mold Temperature: 70 to 80.0°C
Drying Time: 4hrs
Melt Temperature: 260°C
Rear - Zone 1 Temperature: 205 to 215.0°C
Drying Temperature: 80°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.