LNP™ THERMOCOMP™ Compound PFB91S - Americas

Want to keep this datasheet? Save it now in your required format

Description

LNP THERMOCOMP PFB91S is a compound based on Nylon 6 resin containing Proprietary Filler(s).

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.57 g/cm³

Show Supplier Material materials with Density of 1.57 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

7.49 GPa

Show Supplier Material materials with Elastic modulus of 7.49 GPa

ASTM D 638 | 50 mm/min

Elongation

23.0 °C

2.7 %

Show Supplier Material materials with Elongation of 2.7 %

ASTM D 638 | break

Flexural modulus

23.0 °C

6.04 GPa

Show Supplier Material materials with Flexural modulus of 6.04 GPa

ASTM D 790

Impact strength, Izod notched

23.0 °C

37 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 37 kJ/m²

ASTM D 256 | notched, 23°C

Impact strength, Izod notched, ASTM

23.0 °C

37 J/m

Show Supplier Material materials with Impact strength, Izod notched, ASTM of 37 J/m

ASTM D 256 | notched, 23°C

Impact strength, Izod unnotched, ASTM

23.0 °C

283 J/m

Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 283 J/m

ASTM D 4812 | 23°C

Tensile strength

23.0 °C

62 MPa

Show Supplier Material materials with Tensile strength of 62 MPa

ASTM D 638 | brk, Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

163 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 163 °C

ASTM D 648 | 3.2mm, unannealed

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.6 %

Show Supplier Material materials with Shrinkage of 0.6 %

ASTM D 955 | 24 hrs

Technological properties

Property
Availability

Asia,Americas

Features

Low Warpage, Structural

Processing methods

Maximum Moisture Content: 0.15 to 0.25%
Middle - Zone 2 Temperature: 250 to 260.0°C
Screw Speed: 30 to 60.0rpm
Mold Temperature: 80 to 95.0°C
Drying Temperature: 80°C
Rear - Zone 1 Temperature: 240 to 250.0°C
Back Pressure: 0.2 to 0.3MPa
Drying Time: 4hrs
Front - Zone 3 Temperature: 260 to 270.0°C
Melt Temperature: 265 to 270.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.