Description

LNP LUBRICOMP* JX91198 is a compound based on Polyethersulfone resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Coefficient of friction

0.34 [-]

Show Supplier Material materials with Coefficient of friction of 0.34 [-]

Coefficient of friction, kinetic

0.34 [-]

Show Supplier Material materials with Coefficient of friction, kinetic of 0.34 [-]

ASTM D 3702 Modified: Manual

Coefficient of friction, static

0.34 [-]

Show Supplier Material materials with Coefficient of friction, static of 0.34 [-]

ASTM D 3702 Modified: Manual

Density

23.0 °C

1.5 g/cm³

Show Supplier Material materials with Density of 1.5 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

1.6 %

Show Supplier Material materials with Elongation of 1.6 %

ISO 527 | break, 5 mm/min

Flexural modulus

23.0 °C

6.3 GPa

Show Supplier Material materials with Flexural modulus of 6.3 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

140 MPa

Show Supplier Material materials with Flexural strength of 140 MPa

ISO 178 | break, 2 mm/min

Impact strength, Izod notched

23.0 °C

6 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m²

ISO 180/1A | notched 80*10*4, 23°C

Impact strength, Izod unnotched

23.0 °C

26 kJ/m²

Show Supplier Material materials with Impact strength, Izod unnotched of 26 kJ/m²

ISO 180/1U | 80*10*4, 23°C

Tensile strength

23.0 °C

112 MPa

Show Supplier Material materials with Tensile strength of 112 MPa

ISO 527 | break

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 %

SABIC method | on tensile bar

Technological properties

Property
Application areas

Gear/Bearing/Slider

Availability

Europe,Americas

Features

Structural, Wear and Friction

Processing methods

Drying Time: 4hrs
Maximum Moisture Content: 0.05%
Melt Temperature: 355 to 370.0°C
Front - Zone 3 Temperature: 370 to 380.0°C
Middle - Zone 2 Temperature: 360 to 370.0°C
Rear - Zone 1 Temperature: 345 to 355.0°C
Mold Temperature: 140 to 150.0°C
Back Pressure: 0.3 to 0.7MPa
Screw Speed: 60 to 100.0rpm
Drying Temperature: 120 to 150.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.