ULTEM™ Resin AUR200G0 - Europe

Want to keep this datasheet? Save it now in your required format


AUR200G0 is an unreinforced ULTEM recycle based grade.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.





23.0 °C

1.27 g/cm³

Show Supplier Material materials with Density of 1.27 g/cm³

ISO 1183



Elastic modulus

23.0 °C

2.5 GPa

Show Supplier Material materials with Elastic modulus of 2.5 GPa

ISO 527 | 1 mm/min


23.0 °C

5 %

Show Supplier Material materials with Elongation of 5 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

2.6 GPa

Show Supplier Material materials with Flexural modulus of 2.6 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

120 MPa

Show Supplier Material materials with Flexural strength of 120 MPa

ISO 178 | yield, 2 mm/min

Tensile strength

23.0 °C

90 MPa

Show Supplier Material materials with Tensile strength of 90 MPa

ISO 527 | yield, 50 mm/min



Heat deflection temperature, 0.45 MPa

205 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 205 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Rheological Properties


Melt volume-flow rate

18 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 18 cm³/10min

ISO 1133 | MVR at 360°C/5.0 kg

Technological properties

Application areas

Automotive , Structural Support, Vending Machine, Non-LED Lighting, LED Lighting, ATM/Ticket Machine, Building Element, Exhaust System, Electrical




High Heat Resistance, Good dimensional stability

Processing methods

Drying Temperature: 150°C
Drying Time: 4 to 6.0hrs
Maximum Moisture Content: 0.02%
Melt Temperature: 370 to 410.0°C
Nozzle Temperature: 350 to 405.0°C
Front - Zone 3 Temperature: 360 to 415.0°C
Middle - Zone 2 Temperature: 350 to 405.0°C
Rear - Zone 1 Temperature: 340 to 395.0°C
Hopper Temperature: 80 to 120.0°C
Mold Temperature: 140 to 180.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.