Dianhydrides & Imides 1000F3SP - Americas

Want to keep this datasheet? Save it now in your required format

Description

ULTEMTM 1000F3SP powder is a RoHS compliant polyetherimide (PEI) powder offering a glass transition temperature (Tg) of 217ºC. This FDA compliant powder is available in a spherical shape with an average particle size (D50) of 15 micron and a maximum particle size (D100) of 75 micron.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Bulk density

23.0 °C

0.78 g/cm³

Show Supplier Material materials with Bulk density of 0.78 g/cm³

ASTM D 1895

Limiting oxygen index

23.0 °C

47 %

Show Supplier Material materials with Limiting oxygen index of 47 %

Water absorption

23.0 °C

1.25 %

Show Supplier Material materials with Water absorption of 1.25 %

ASTM D 570 | (23°C/Saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.58 GPa

Show Supplier Material materials with Elastic modulus of 3.58 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

7 %

Show Supplier Material materials with Elongation of 7 %

ASTM D 638 | yld, Type I, 5 mm/min

Flexural modulus

23.0 °C

3.3 GPa

Show Supplier Material materials with Flexural modulus of 3.3 GPa

ASTM D 790 | 2.6 mm/min, 100 mm span

Flexural strength

23.0 °C

151 MPa

Show Supplier Material materials with Flexural strength of 151 MPa

ASTM D 790 | yld, 2.6 mm/min, 100 mm span

Hardness, Rockwell M

23.0 °C

109 [-]

Show Supplier Material materials with Hardness, Rockwell M of 109 [-]

ASTM D 785 |

Impact strength, Izod notched

23.0 °C

53 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 53 kJ/m²

ASTM D 256 | notched, 23°C

Taber Abrasion

23.0 °C

10 mg/1000cy

Show Supplier Material materials with Taber Abrasion of 10 mg/1000cy

ASTM D 1044 | CS-17, 1 kg

Tensile strength

23.0 °C

110 MPa

Show Supplier Material materials with Tensile strength of 110 MPa

ASTM D 638 | yld, Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5.58E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 5.58E-5 1/K

ASTM E 831 | -20°C to 150°C

Coefficient of thermal expansion, transverse

23.0 °C

5.4E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5.4E-5 1/K

ASTM E 831 | -20°C to 150°C

Heat deflection temperature

201 - 210 °C

Show Supplier Material materials with Heat deflection temperature of 201 - 210 °C

Heat deflection temperature, 0.45 MPa

210 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 210 °C

ASTM D 648 | 6.4 mm, unannealed

Heat deflection temperature, 1.80 MPa

201 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 201 °C

ASTM D 648 | 6.4 mm, unannealed

Thermal conductivity

23.0 °C

0.22 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.22 W/(m·K)

ASTM C177

Vicat softening temperature

218 °C

Show Supplier Material materials with Vicat softening temperature of 218 °C

ASTM D 1525 | Rate B/50

Electrical

PropertyTemperatureValueComment

Dielectric strength

23.0 °C

28 kV/mm

Show Supplier Material materials with Dielectric strength of 28 kV/mm

ASTM D 149 | in oil, 1.6 mm

Dissipation factor

23.0 °C

2.5E-3 [-]

Show Supplier Material materials with Dissipation factor of 2.5E-3 [-]

ASTM D 150 | 2450 MHz

Volume resistivity

23.0 °C

1.00E+17 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm

ASTM D 257

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | on tensile bar

Technological properties

Property
Application areas

Composite

Availability

Europe,Americas

Processing methods

Screw Speed: 40 to 70.0rpm
Middle - Zone 2 Temperature: 340 to 400.0°C
Shot to Cylinder Size: 40 to 60.0%
Melt Temperature: 350 to 400.0°C
Drying Temperature: 150°C
Drying Time: 4 to 6.0hrs
Rear - Zone 1 Temperature: 330 to 400.0°C
Drying Time (Cumulative): 24hrs
Front - Zone 3 Temperature: 345 to 400.0°C
Back Pressure: 0.3 to 0.7MPa
Vent Depth: 0.025 to 0.076mm
Maximum Moisture Content: 0.02%
Mold Temperature: 135 to 165.0°C
Nozzle Temperature: 345 to 400.0°C

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.