Dianhydrides & Imides 1000F3SP - Europe

Want to keep this datasheet? Save it now in your required format

Description

ULTEMTM 1000F3SP powder is a RoHS compliant polyetherimide (PEI) powder offering a glass transition temperature (Tg) of 217ºC. This FDA compliant powder is available in a spherical shape with an average particle size (D50) of 15 micron and a maximum particle size (D100) of 75 micron.

This material data has been provided by Sabic.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Bulk density

23.0 °C

0.78 g/cm³

Show Supplier Material materials with Bulk density of 0.78 g/cm³

ISO 1183

Limiting oxygen index

23.0 °C

47 %

Show Supplier Material materials with Limiting oxygen index of 47 %

Water absorption

23.0 °C

1.25 %

Show Supplier Material materials with Water absorption of 1.25 %

ISO 62-1 | (23°C/saturated)

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.2 GPa

Show Supplier Material materials with Elastic modulus of 3.2 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

6 %

Show Supplier Material materials with Elongation of 6 %

ISO 527 | yield, 50 mm/min

Flexural modulus

23.0 °C

3.3 GPa

Show Supplier Material materials with Flexural modulus of 3.3 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

160 MPa

Show Supplier Material materials with Flexural strength of 160 MPa

ISO 178 | yield, 2 mm/min

Hardness, Rockwell M

23.0 °C

109 [-]

Show Supplier Material materials with Hardness, Rockwell M of 109 [-]

ASTM D 785 |

Impact strength, Izod notched

23.0 °C

6 kJ/m²

Show Supplier Material materials with Impact strength, Izod notched of 6 kJ/m²

ISO 180/1A | notched 80*10*4, 23°C

Taber Abrasion

23.0 °C

10 mg/1000cy

Show Supplier Material materials with Taber Abrasion of 10 mg/1000cy

ASTM D 1044 | CS-17, 1 kg

Tensile strength

23.0 °C

105 MPa

Show Supplier Material materials with Tensile strength of 105 MPa

ISO 527 | yield, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 5E-5 1/K

ISO 11359-2 | 23°C to 150°C

Coefficient of thermal expansion, transverse

23.0 °C

5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 5E-5 1/K

ISO 11359-2 | 23°C to 150°C

Heat deflection temperature

190 - 200 °C

Show Supplier Material materials with Heat deflection temperature of 190 - 200 °C

Heat deflection temperature, 0.45 MPa

200 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 200 °C

ISO 75/Be | Edgew 120*10*4 sp=100mm

Heat deflection temperature, 1.80 MPa

190 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 190 °C

ISO 75/Ae | Edgew 120*10*4 sp=100mm

Thermal conductivity

23.0 °C

0.24 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.24 W/(m·K)

ISO 8302

Vicat softening temperature

211 °C

Show Supplier Material materials with Vicat softening temperature of 211 °C

ISO 306 | Rate B/50

Electrical

PropertyTemperatureValueComment

Dielectric strength

23.0 °C

16 kV/mm

Show Supplier Material materials with Dielectric strength of 16 kV/mm

IEC 60243-1 | in oil, 3.2 mm,

Dissipation factor

23.0 °C

2.5E-3 [-]

Show Supplier Material materials with Dissipation factor of 2.5E-3 [-]

IEC 60250 | 2450 MHz

Volume resistivity

23.0 °C

1.00E+15 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm

IEC 60093 |

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Composite

Availability

Europe,Americas

Processing methods

Nozzle Temperature: 345 to 400.0°C
Mold Temperature: 135 to 165.0°C
Back Pressure: 0.3 to 0.7MPa
Rear - Zone 1 Temperature: 330 to 400.0°C
Maximum Moisture Content: 0.02%
Melt Temperature: 350 to 400.0°C
Front - Zone 3 Temperature: 345 to 400.0°C
Drying Time: 4 to 6.0hrs
Vent Depth: 0.025 to 0.076mm
Screw Speed: 40 to 70.0rpm
Drying Time (Cumulative): 24hrs
Drying Temperature: 150°C
Middle - Zone 2 Temperature: 340 to 400.0°C
Shot to Cylinder Size: 40 to 60.0%

Supplier Disclaimer

While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.