| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.1 g/cm³ Show Supplier Material materials with Density of 8.1 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 207 GPa Show Supplier Material materials with Elastic modulus of 207 GPa | Annealed condition |
100.0 °C | 202 GPa Show Supplier Material materials with Elastic modulus of 202 GPa | Annealed condition | |
200.0 °C | 197 GPa Show Supplier Material materials with Elastic modulus of 197 GPa | Annealed condition | |
300.0 °C | 191 GPa Show Supplier Material materials with Elastic modulus of 191 GPa | Annealed condition | |
400.0 °C | 185 GPa Show Supplier Material materials with Elastic modulus of 185 GPa | Annealed condition | |
500.0 °C | 178 GPa Show Supplier Material materials with Elastic modulus of 178 GPa | Annealed condition | |
600.0 °C | 170 GPa Show Supplier Material materials with Elastic modulus of 170 GPa | Annealed condition | |
700.0 °C | 161 GPa Show Supplier Material materials with Elastic modulus of 161 GPa | Annealed condition | |
800.0 °C | 150 GPa Show Supplier Material materials with Elastic modulus of 150 GPa | Annealed condition | |
900.0 °C | 138 GPa Show Supplier Material materials with Elastic modulus of 138 GPa | Annealed condition | |
1000.0 °C | 125 GPa Show Supplier Material materials with Elastic modulus of 125 GPa | Annealed condition | |
Elongation A2 | 23.0 °C | 30 % Show Supplier Material materials with Elongation A2 of 30 % | min. |
Tensile strength | 23.0 °C | 550 - 760 MPa Show Supplier Material materials with Tensile strength of 550 - 760 MPa | |
Yield strength Rp0.2 | 23.0 °C | 205 MPa Show Supplier Material materials with Yield strength Rp0.2 of 205 MPa | min. |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.38E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.38E-5 1/K | for 30°C to the mentioned temperature |
200.0 °C | 1.44E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.44E-5 1/K | for 30°C to the mentioned temperature | |
300.0 °C | 1.46E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.46E-5 1/K | for 30°C to the mentioned temperature | |
400.0 °C | 1.48E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.48E-5 1/K | for 30°C to the mentioned temperature | |
500.0 °C | 1.52E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.52E-5 1/K | for 30°C to the mentioned temperature | |
600.0 °C | 1.56E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.56E-5 1/K | for 30°C to the mentioned temperature | |
700.0 °C | 1.61E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.61E-5 1/K | for 30°C to the mentioned temperature | |
800.0 °C | 1.67E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.67E-5 1/K | for 30°C to the mentioned temperature | |
900.0 °C | 1.72E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.72E-5 1/K | for 30°C to the mentioned temperature | |
1000.0 °C | 1.78E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.78E-5 1/K | for 30°C to the mentioned temperature | |
Specific heat capacity | 20.0 °C | 448 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 448 J/(kg·K) | |
100.0 °C | 469 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 469 J/(kg·K) | ||
200.0 °C | 498 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 498 J/(kg·K) | ||
300.0 °C | 523 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 523 J/(kg·K) | ||
400.0 °C | 548 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 548 J/(kg·K) | ||
500.0 °C | 578 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 578 J/(kg·K) | ||
600.0 °C | 603 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 603 J/(kg·K) | ||
700.0 °C | 632 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 632 J/(kg·K) | ||
800.0 °C | 657 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 657 J/(kg·K) | ||
900.0 °C | 686 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 686 J/(kg·K) | ||
1000.0 °C | 712 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 712 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 11.2 W/(m·K) Show Supplier Material materials with Thermal conductivity of 11.2 W/(m·K) | |
100.0 °C | 12.7 W/(m·K) Show Supplier Material materials with Thermal conductivity of 12.7 W/(m·K) | ||
200.0 °C | 14.3 W/(m·K) Show Supplier Material materials with Thermal conductivity of 14.3 W/(m·K) | ||
300.0 °C | 16 W/(m·K) Show Supplier Material materials with Thermal conductivity of 16 W/(m·K) | ||
400.0 °C | 17.7 W/(m·K) Show Supplier Material materials with Thermal conductivity of 17.7 W/(m·K) | ||
500.0 °C | 19.5 W/(m·K) Show Supplier Material materials with Thermal conductivity of 19.5 W/(m·K) | ||
600.0 °C | 21 W/(m·K) Show Supplier Material materials with Thermal conductivity of 21 W/(m·K) | ||
700.0 °C | 22.8 W/(m·K) Show Supplier Material materials with Thermal conductivity of 22.8 W/(m·K) | ||
800.0 °C | 24.4 W/(m·K) Show Supplier Material materials with Thermal conductivity of 24.4 W/(m·K) | ||
900.0 °C | 26.1 W/(m·K) Show Supplier Material materials with Thermal conductivity of 26.1 W/(m·K) | ||
1000.0 °C | 27.8 W/(m·K) Show Supplier Material materials with Thermal conductivity of 27.8 W/(m·K) | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 1.18E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.18E-6 Ω·m |
100.0 °C | 1.19E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.19E-6 Ω·m | |
200.0 °C | 1.21E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.21E-6 Ω·m | |
300.0 °C | 1.22E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.22E-6 Ω·m | |
400.0 °C | 1.23E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.23E-6 Ω·m | |
500.0 °C | 1.24E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.24E-6 Ω·m | |
600.0 °C | 1.25E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.25E-6 Ω·m | |
700.0 °C | 1.25E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.25E-6 Ω·m | |
800.0 °C | 1.25E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.25E-6 Ω·m | |
900.0 °C | 1.26E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.26E-6 Ω·m | |
1000.0 °C | 1.26E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.26E-6 Ω·m | |
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Aluminium | 1.3 % Show Supplier Material materials with Aluminium of 1.3 % | ||
Carbon | 0.03 % Show Supplier Material materials with Carbon of 0.03 % | ||
Chromium | 23 % Show Supplier Material materials with Chromium of 23 % | ||
Iron | Balance | ||
Manganese | 0.6 % Show Supplier Material materials with Manganese of 0.6 % | ||
Nickel | 60 % Show Supplier Material materials with Nickel of 60 % | ||
Phosphorus | 0.03 % Show Supplier Material materials with Phosphorus of 0.03 % | max. | |
Silicon | 0.3 % Show Supplier Material materials with Silicon of 0.3 % | ||
Sulfur | 0.015 % Show Supplier Material materials with Sulfur of 0.015 % | max. | |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Sanicro® 61 is a general-purpose, highly corrosion resistant alloy suitable for a wide range of high temperature applications such as: | |
| Corrosion properties | Sanicro® 61 has superior resistance to, in particular, oxidation at high temperatures up to 1200°C (2200°F). The grade also offers excellent resistance to oxide scaling under cyclic thermal conditions, largely owing to the addition of aluminium. | |
| Other | Forms of supply: Sanicro® 61 seamless nickel alloy tubing is supplied bright annealed in the outside diameter range 27.67-48.3 mm (0.75-1.5 in. nominal) and wall-thickness range 2.0-4.0 mm (0.079-0.160 in.). Tolerances | |
| Welding | The weldability of Sanicro® 61 is good. Suitable methods of fusion welding are manual metal-arc welding (MMA/SMAW) and gas-shielded arc welding, with the TIG/GTAW method as first choice. For Sanicro® 61, heat-input of <1.2 kJ/mm and interpass temperature of <100°C (210°F) are recommended. A string bead welding technique should be used. Recommended filler metals:
| |