General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8 g/cm³ Show Supplier Material materials with Density of 8 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 20.0 °C | 200 GPa Show Supplier Material materials with Elastic modulus of 200 GPa | |
400.0 °C | 175 GPa Show Supplier Material materials with Elastic modulus of 175 GPa | ||
600.0 °C | 160 GPa Show Supplier Material materials with Elastic modulus of 160 GPa | ||
Elongation A2 | 23.0 °C | 30 % Show Supplier Material materials with Elongation A2 of 30 % | min. |
Hardness, Vickers | 23.0 °C | 150 [-] Show Supplier Material materials with Hardness, Vickers of 150 [-] | |
Tensile strength | 23.0 °C | 520 - 689 MPa Show Supplier Material materials with Tensile strength of 520 - 689 MPa | |
Yield strength Rp0.1 | 20.0 °C | 210 MPa Show Supplier Material materials with Yield strength Rp0.1 of 210 MPa | min. |
100.0 °C | 215 MPa Show Supplier Material materials with Yield strength Rp0.1 of 215 MPa | min. | |
200.0 °C | 195 MPa Show Supplier Material materials with Yield strength Rp0.1 of 195 MPa | min. | |
300.0 °C | 185 MPa Show Supplier Material materials with Yield strength Rp0.1 of 185 MPa | min. | |
400.0 °C | 180 MPa Show Supplier Material materials with Yield strength Rp0.1 of 180 MPa | min. | |
500.0 °C | 170 MPa Show Supplier Material materials with Yield strength Rp0.1 of 170 MPa | min. | |
600.0 °C | 165 MPa Show Supplier Material materials with Yield strength Rp0.1 of 165 MPa | min. | |
Yield strength Rp0.2 | 20.0 °C | 207 MPa Show Supplier Material materials with Yield strength Rp0.2 of 207 MPa | min. |
100.0 °C | 190 MPa Show Supplier Material materials with Yield strength Rp0.2 of 190 MPa | min. | |
200.0 °C | 175 MPa Show Supplier Material materials with Yield strength Rp0.2 of 175 MPa | min. | |
300.0 °C | 165 MPa Show Supplier Material materials with Yield strength Rp0.2 of 165 MPa | min. | |
400.0 °C | 160 MPa Show Supplier Material materials with Yield strength Rp0.2 of 160 MPa | min. | |
500.0 °C | 150 MPa Show Supplier Material materials with Yield strength Rp0.2 of 150 MPa | min. | |
600.0 °C | 145 MPa Show Supplier Material materials with Yield strength Rp0.2 of 145 MPa | min. | |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.6E-5 1/K | for 20°C to the mentioned temperature |
200.0 °C | 1.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.6E-5 1/K | for 20°C to the mentioned temperature | |
300.0 °C | 1.6E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.6E-5 1/K | for 20°C to the mentioned temperature | |
400.0 °C | 1.65E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.65E-5 1/K | for 20°C to the mentioned temperature | |
500.0 °C | 1.65E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.65E-5 1/K | for 20°C to the mentioned temperature | |
600.0 °C | 1.7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.7E-5 1/K | for 20°C to the mentioned temperature | |
Specific heat capacity | 20.0 °C | 475 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 475 J/(kg·K) | |
100.0 °C | 500 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 500 J/(kg·K) | ||
200.0 °C | 515 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 515 J/(kg·K) | ||
300.0 °C | 525 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 525 J/(kg·K) | ||
400.0 °C | 525 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 525 J/(kg·K) | ||
500.0 °C | 535 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 535 J/(kg·K) | ||
600.0 °C | 585 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 585 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 12 W/(m·K) Show Supplier Material materials with Thermal conductivity of 12 W/(m·K) | |
100.0 °C | 14 W/(m·K) Show Supplier Material materials with Thermal conductivity of 14 W/(m·K) | ||
200.0 °C | 16 W/(m·K) Show Supplier Material materials with Thermal conductivity of 16 W/(m·K) | ||
300.0 °C | 17 W/(m·K) Show Supplier Material materials with Thermal conductivity of 17 W/(m·K) | ||
400.0 °C | 18 W/(m·K) Show Supplier Material materials with Thermal conductivity of 18 W/(m·K) | ||
500.0 °C | 20 W/(m·K) Show Supplier Material materials with Thermal conductivity of 20 W/(m·K) | ||
600.0 °C | 23 W/(m·K) Show Supplier Material materials with Thermal conductivity of 23 W/(m·K) | ||
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 20.0 °C | 9.9E-7 Ω·m Show Supplier Material materials with Electrical resistivity of 9.9E-7 Ω·m |
100.0 °C | 1.01E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.01E-6 Ω·m | |
200.0 °C | 1.03E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.03E-6 Ω·m | |
300.0 °C | 1.05E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.05E-6 Ω·m | |
400.0 °C | 1.08E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.08E-6 Ω·m | |
500.0 °C | 1.12E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.12E-6 Ω·m | |
600.0 °C | 1.18E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 1.18E-6 Ω·m | |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Aluminium | 0.3 % Show Supplier Material materials with Aluminium of 0.3 % | ||
Carbon | 0.03 % Show Supplier Material materials with Carbon of 0.03 % | max. | |
Chromium | 20 % Show Supplier Material materials with Chromium of 20 % | ||
Cobalt | 0.1 % Show Supplier Material materials with Cobalt of 0.1 % | Lower contents can be specified after agreement. | |
Copper | 0.1 % Show Supplier Material materials with Copper of 0.1 % | max. | |
Iron | Balance | ||
Manganese | 0.6 % Show Supplier Material materials with Manganese of 0.6 % | ||
Nickel | 32 % Show Supplier Material materials with Nickel of 32 % | ||
Phosphorus | 0.02 % Show Supplier Material materials with Phosphorus of 0.02 % | max. | |
Silicon | 0.5 % Show Supplier Material materials with Silicon of 0.5 % | ||
Sulfur | 0.015 % Show Supplier Material materials with Sulfur of 0.015 % | max. | |
Titanium | 0.5 % Show Supplier Material materials with Titanium of 0.5 % |
Technological properties
Property | ||
---|---|---|
Certifications | Approvals: Approved for use according to ASME Boiler and Pressure Vessel Code Section III, division 1 and Section VIII, division 1 and 2 | |
Cold Forming | Heat treatment after cold bending is not normally necessary, but this point must be decided with regard to the degree of bending and the operating conditions. Heat treatment, if any, should take the form of stress relieving or solution annealing. | |
Corrosion properties | General corrosion: Sanicro® 30 has approximately the same resistance to organic and inorganic acids as steel of the ASTM TP 304 type. Its resistance to sodium hydroxide is very good except at the very highest concentrations and temperatures. Pitting: The material has somewhat better resistance to pitting than steel of the ASTM TP 304 type. Intergranular corrosion and stress corrosion cracking: In comparison with the standard Alloy 800, Sanicro® 30 has improved resistance both to intergranular corrosion and to intergranular stress corrosion cracking. This is obtained by a high degree of stabilization and a production sequence giving a small grain size. The resistance to trans- granular stress corrosion cracking is very good as for all high-nickel alloys. Gas corrosion: In general this grade is not used at temperatures high enough for gas corrosion to be a problem. For such cases the appropriate metal to choose is Sanicro® 31HT. However, compared with Sanicro® 31HT, Sanicro® 30 has about the same resistance to gas corrosion. | |
Heat Treatment | The tubes are delivered in heat treated condition. If another treatment is needed after further processing the following is recommended. Stress relieving: 800-875°C (1470-1605°F), 10-15 minutes, cooling in air. Solution annealing: 950-1050°C (1740-1920°F), 1-10 minutes, rapid cooling in water or air. | |
Hot forming | Hot bending is carried out at 1050-850°C (1920-1560°F) and should be followed by solution annealing. | |
Other | Forms of supply: Tube and pipe are supplied hot- or cold-worked, solution-annealed and white-pickled or bright-annealed. The principal size range can be seen from the figure on the right, but also certain sizes can be delivered on request. | |
Welding | The weldability of Sanicro® 30 is good. Suitable methods of fusion welding are manual metal-arc welding (MMA/SMAW) and gas-shielded arc welding, with the TIG/GTAW method as first choice. Since the material has low thermal conductivity and high thermal expansion. Welding plans should therefore be carefully selected in advance, so that distortions of the welded joint are minimized. If residual stresses are a concern, solution annealing can be performed after welding. For Sanicro® 30, heat-input of <1.0 kJ/mm and interpass temperature of <100°C (210°F) are recommended. A string bead welding technique should be used. Recommended filler metals:
|