General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.57 g/cm³ Show Supplier Material materials with Density of 1.57 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.02 % Show Supplier Material materials with Water absorption of 0.02 % | ISO 62 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 1.9 % Show Supplier Material materials with Elongation of 1.9 % | ISO 527 |
Flexural modulus | 23.0 °C | 11 GPa Show Supplier Material materials with Flexural modulus of 11 GPa | ISO 178 |
Flexural strength | 23.0 °C | 250 MPa Show Supplier Material materials with Flexural strength of 250 MPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179 |
Tensile strength | 23.0 °C | 160 MPa Show Supplier Material materials with Tensile strength of 160 MPa | ISO 527 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 260 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 260 °C | ISO 75 | |
Max service temperature | 260 °C Show Supplier Material materials with Max service temperature of 260 °C | ||
Melting point | 280 °C Show Supplier Material materials with Melting point of 280 °C | ISO 11357 (10°C/min) | |
Flammability | V-0, UL-94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 125 V Show Supplier Material materials with Comparative tracking index of 125 V | IEC 60112 |
Dielectric constant | 23.0 °C | 4 [-] Show Supplier Material materials with Dielectric constant of 4 [-] | IEC 60250 |
Dielectric strength | 23.0 °C | 16 kV/mm Show Supplier Material materials with Dielectric strength of 16 kV/mm | IEC 60243 |
Dissipation factor | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor of 2E-3 [-] | IEC 60250 |
Volume resistivity | 23.0 °C | 2.40E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 2.40E+15 Ω·cm | IEC 60093 |
Technological properties
Property | ||
---|---|---|
Application areas | In the electronics industry for the production of connectors, wiring device, frequency divider and a variety of instrument components, such as shell; in the aerospace industry for the production of high strength, high temperature resistant and insulation of the high performance requirements of thin-walled parts; in the chemical industry for the production of corrosion-resistant valves, insulation devices in military products, for the production of precision electrical connectors, high strength, high temperature resistant contactor shell, motor module, pump impeller, pump, chemical pump etc. | |
Fillers | 30% Glass Fiber | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |