PPS CF10 SGC101S41

Alternative and trade names
PPS-SGC101S41
Want to keep this datasheet? Save it now in your required format

Description

It is a 10% carbon fiber reinforced linear polyphenylene sulfide,filler with PTFE developed to provide low friction coefficient, low wear.

This material data has been provided by Sciengy New Materials Co. Ltd.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.38 g/cm³

Show Supplier Material materials with Density of 1.38 g/cm³

ISO 1183

Water absorption

23.0 °C

0.04 %

Show Supplier Material materials with Water absorption of 0.04 %

ISO 62

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

1.2 %

Show Supplier Material materials with Elongation of 1.2 %

ISO 527

Flexural modulus

23.0 °C

11 GPa

Show Supplier Material materials with Flexural modulus of 11 GPa

ISO 178

Flexural strength

23.0 °C

235 MPa

Show Supplier Material materials with Flexural strength of 235 MPa

ISO 178

Impact strength, Charpy notched

23.0 °C

6 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 6 kJ/m²

ISO 179

Tensile strength

23.0 °C

155 MPa

Show Supplier Material materials with Tensile strength of 155 MPa

ISO 527

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

255 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 255 °C

ISO 75

Max service temperature

255 °C

Show Supplier Material materials with Max service temperature of 255 °C

Melting point

280 °C

Show Supplier Material materials with Melting point of 280 °C

ISO 11357 (10°C/min)

Flammability

V-0, UL-94

Technological properties

Property
Application areas

Can be produced Bearing seat, the aircraft shell, dashboard, universal head, sealing parts

Fillers

10% Carbon Fiber and PTFE

Processing methods

Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min