General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.44 g/cm³ Show Supplier Material materials with Density of 1.44 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.04 % Show Supplier Material materials with Water absorption of 0.04 % | ISO 62 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 1.3 % Show Supplier Material materials with Elongation of 1.3 % | ISO 527 |
Flexural modulus | 23.0 °C | 23 GPa Show Supplier Material materials with Flexural modulus of 23 GPa | ISO 178 |
Flexural strength | 23.0 °C | 310 MPa Show Supplier Material materials with Flexural strength of 310 MPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO 179 |
Tensile strength | 23.0 °C | 210 MPa Show Supplier Material materials with Tensile strength of 210 MPa | ISO 527 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 265 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 265 °C | ISO 75 | |
Max service temperature | 265 °C Show Supplier Material materials with Max service temperature of 265 °C | ||
Melting point | 280 °C Show Supplier Material materials with Melting point of 280 °C | ISO 11357 (10°C/min) | |
Flammability | V-0, UL-94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Volume resistivity | 23.0 °C | 2000 Ω·cm Show Supplier Material materials with Volume resistivity of 2000 Ω·cm | IEC 60093 |
Technological properties
Property | ||
---|---|---|
Application areas | Can be produced Bearing seat, the aircraft shell, dashboard, universal head, sealing parts | |
Fillers | 30% Carbon Fiber | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |