PPS GF PA66 SG401T87

Alternative and trade names
AS-SG401T87
Want to keep this datasheet? Save it now in your required format

Description

It is a glass fiber reinforced by PPS based PA66 alloy to provide excellent mechanical strength, toughness and rigidity, along with excellent flow in thin-walled parts, low flash characteristics, and fast cycle times. It may be easily molded in conventional injection molding equipment utilizing water heated molds.

This material data has been provided by Sciengy New Materials Co. Ltd.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.55 g/cm³

Show Supplier Material materials with Density of 1.55 g/cm³

ISO 1183

Water absorption

23.0 °C

0.2 %

Show Supplier Material materials with Water absorption of 0.2 %

ISO 62

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

2 %

Show Supplier Material materials with Elongation of 2 %

ISO 527

Flexural modulus

23.0 °C

12 GPa

Show Supplier Material materials with Flexural modulus of 12 GPa

ISO 178

Flexural strength

23.0 °C

270 MPa

Show Supplier Material materials with Flexural strength of 270 MPa

ISO 178

Impact strength, Charpy notched

23.0 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²

ISO 179

Tensile strength

23.0 °C

190 MPa

Show Supplier Material materials with Tensile strength of 190 MPa

ISO 527

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

250 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 250 °C

ISO 75

Max service temperature

250 °C

Show Supplier Material materials with Max service temperature of 250 °C

Melting point

280 °C

Show Supplier Material materials with Melting point of 280 °C

ISO 11357 (10°C/min)

Flammability

HB, UL-94

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

270 V

Show Supplier Material materials with Comparative tracking index of 270 V

IEC 60112

Dielectric constant

23.0 °C

4 [-]

Show Supplier Material materials with Dielectric constant of 4 [-]

IEC 60250

Dielectric strength

23.0 °C

22 kV/mm

Show Supplier Material materials with Dielectric strength of 22 kV/mm

IEC 60243

Dissipation factor

23.0 °C

3E-3 [-]

Show Supplier Material materials with Dissipation factor of 3E-3 [-]

IEC 60250

Volume resistivity

23.0 °C

1.00E+15 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm

IEC 60093

Technological properties

Property
Application areas

Can be used in the production of Aluminum Alloy fixture, mixing warter valve, water heater set of water treatment equipment, and other products in the field of high toughness

Fillers

Glass Fiber

Processing methods

Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min