PPS GF PA66 SG401A63

Alternative and trade names
AS-SG401A63
Want to keep this datasheet? Save it now in your required format

Description

It is a glass fiber reinforced by PPS based PA66 alloy to provide excellent mechanical strength, toughness and rigidity, along with excellent flow in thin-walled parts, low flash characteristics, and fast cycle times. It may be easily molded in conventional injection molding equipment utilizing water heated molds.

This material data has been provided by Sciengy New Materials Co. Ltd.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.51 g/cm³

Show Supplier Material materials with Density of 1.51 g/cm³

ISO 1183

Water absorption

23.0 °C

0.2 %

Show Supplier Material materials with Water absorption of 0.2 %

ISO 62

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

2 %

Show Supplier Material materials with Elongation of 2 %

ISO 527

Flexural modulus

23.0 °C

11 GPa

Show Supplier Material materials with Flexural modulus of 11 GPa

ISO 178

Flexural strength

23.0 °C

255 MPa

Show Supplier Material materials with Flexural strength of 255 MPa

ISO 178

Impact strength, Charpy notched

23.0 °C

13 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m²

ISO 179

Tensile strength

23.0 °C

155 MPa

Show Supplier Material materials with Tensile strength of 155 MPa

ISO 527

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

240 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 240 °C

ISO 75

Melting point

280 °C

Show Supplier Material materials with Melting point of 280 °C

ISO 11357 (10°C/min)

Flammability

HB, UL-94

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

170 V

Show Supplier Material materials with Comparative tracking index of 170 V

IEC 60112

Dielectric constant

23.0 °C

4 [-]

Show Supplier Material materials with Dielectric constant of 4 [-]

IEC 60250

Dielectric strength

23.0 °C

22 kV/mm

Show Supplier Material materials with Dielectric strength of 22 kV/mm

IEC 60243

Dissipation factor

23.0 °C

3E-3 [-]

Show Supplier Material materials with Dissipation factor of 3E-3 [-]

IEC 60250

Volume resistivity

23.0 °C

1.00E+15 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm

IEC 60093

Technological properties

Property
Application areas

Can be used in the production of Aluminum Alloy fixture, mixing warter valve, water heater set of water treatment equipment, and other products in the field of high toughness

Fillers

Glass Fiber

Processing methods

Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min