PPS CF10 SGC101S21

Alternative and trade names
ES-SGC101S21

Want to keep this datasheet? Save it now in your required format

Description

It is a 10% carbon fiber reinforced PPS/PTFE compound specially formulated to have a low coefficient of friction for use in low surface friction and wear applications

This material data has been provided by Sciengy New Materials Co. Ltd.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.6 g/cm³ Show Supplier Material materials with Density of 1.6 g/cm³	ISO 1183
Water absorption	23.0 °C	0.04 % Show Supplier Material materials with Water absorption of 0.04 %	ISO 62

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	1.2 % Show Supplier Material materials with Elongation of 1.2 %	ISO 527
Flexural modulus	23.0 °C	14 GPa Show Supplier Material materials with Flexural modulus of 14 GPa	ISO 178
Flexural strength	23.0 °C	200 MPa Show Supplier Material materials with Flexural strength of 200 MPa	ISO 178
Impact strength, Charpy notched	23.0 °C	6.5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 6.5 kJ/m²	ISO 179
Tensile strength	23.0 °C	125 MPa Show Supplier Material materials with Tensile strength of 125 MPa	ISO 527

Thermal

Property	Value	Comment
Heat deflection temperature, 1.80 MPa	260 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 260 °C	ISO 75
Melting point	280 °C Show Supplier Material materials with Melting point of 280 °C	ISO 11357 (10°C/min)
Flammability	V-0, UL-94

Technological properties

Property
Application areas	Can be used in the production of gear, bearing, slide and low friction coefficient, low friction consumption
Fillers	10% Carbon Fiber
Processing methods	Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min