PPS GF30 SG301R65

Alternative and trade names
PPS-SG301R65, PPS-I-GF30
Want to keep this datasheet? Save it now in your required format

Description

It is a 30% glass fiber reinforced linear PPS based elastomer alloy that is specially formulated to provide improved ductility and impact strength.

This material data has been provided by Sciengy New Materials Co. Ltd.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.53 g/cm³

Show Supplier Material materials with Density of 1.53 g/cm³

ISO 1183

Water absorption

23.0 °C

0.02 %

Show Supplier Material materials with Water absorption of 0.02 %

ISO 62

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

2.5 %

Show Supplier Material materials with Elongation of 2.5 %

ISO 527

Flexural modulus

23.0 °C

10 GPa

Show Supplier Material materials with Flexural modulus of 10 GPa

ISO 178

Flexural strength

23.0 °C

245 MPa

Show Supplier Material materials with Flexural strength of 245 MPa

ISO 178

Impact strength, Charpy notched

23.0 °C

15 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 15 kJ/m²

ISO 179

Tensile strength

23.0 °C

165 MPa

Show Supplier Material materials with Tensile strength of 165 MPa

ISO 527

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

260 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 260 °C

ISO 75

Melting point

280 °C

Show Supplier Material materials with Melting point of 280 °C

ISO 11357 (10°C/min)

Flammability

V-0, UL-94

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

125 V

Show Supplier Material materials with Comparative tracking index of 125 V

IEC 60112

Dielectric constant

23.0 °C

4 [-]

Show Supplier Material materials with Dielectric constant of 4 [-]

IEC 60250

Dielectric strength

23.0 °C

16 kV/mm

Show Supplier Material materials with Dielectric strength of 16 kV/mm

IEC 60243

Dissipation factor

23.0 °C

2E-3 [-]

Show Supplier Material materials with Dissipation factor of 2E-3 [-]

IEC 60250

Volume resistivity

23.0 °C

2.00E+15 Ω·cm

Show Supplier Material materials with Volume resistivity of 2.00E+15 Ω·cm

IEC 60093

Technological properties

Property
Application areas

Can be used in the production of Aluminum Alloy fixture, mixing warter valve, water heater set of water treatment equipment, and other products in the field of high toughness

Fillers

30% Glass Fiber, linear polyphenylene sulfide and elastomer

Processing methods

Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min