General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.72 g/cm³ Show Supplier Material materials with Density of 1.72 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.02 % Show Supplier Material materials with Water absorption of 0.02 % | ISO 62 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 1 % Show Supplier Material materials with Elongation of 1 % | ISO 527 |
Flexural modulus | 23.0 °C | 18.5 GPa Show Supplier Material materials with Flexural modulus of 18.5 GPa | ISO 178 |
Flexural strength | 23.0 °C | 275 MPa Show Supplier Material materials with Flexural strength of 275 MPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 25 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 25 kJ/m² | ISO 179 |
Tensile strength | 23.0 °C | 170 MPa Show Supplier Material materials with Tensile strength of 170 MPa | ISO 527 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 280 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 280 °C | ISO 75 | |
Flammability | V-0, UL-94 |
Technological properties
Property | ||
---|---|---|
Application areas | Can be used in vacuum pump impeller,oilfield accessories and other components | |
Fillers | 50% Glass Fiber | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |