General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.67 g/cm³ Show Supplier Material materials with Density of 1.67 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.02 % Show Supplier Material materials with Water absorption of 0.02 % | ISO 62 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 1.7 % Show Supplier Material materials with Elongation of 1.7 % | ISO 527 |
Flexural modulus | 23.0 °C | 14 GPa Show Supplier Material materials with Flexural modulus of 14 GPa | ISO 178 |
Flexural strength | 23.0 °C | 265 MPa Show Supplier Material materials with Flexural strength of 265 MPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179 |
Tensile strength | 23.0 °C | 175 MPa Show Supplier Material materials with Tensile strength of 175 MPa | ISO 527 |
Thermal
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 150 V Show Supplier Material materials with Comparative tracking index of 150 V | IEC 60112 |
Dielectric constant | 23.0 °C | 4 [-] Show Supplier Material materials with Dielectric constant of 4 [-] | IEC 60250 |
Dielectric strength | 23.0 °C | 16 kV/mm Show Supplier Material materials with Dielectric strength of 16 kV/mm | IEC 60243 |
Dissipation factor | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor of 2E-3 [-] | IEC 60250 |
Volume resistivity | 23.0 °C | 2.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 2.00E+15 Ω·cm | IEC 60093 |
Technological properties
Property | ||
---|---|---|
Application areas | Can be used in electronics,communications,high-frequency heating industrial equipment and measurement, inspection and test equipment such as the need to engage in electrostatic and electromagnetic shielding and other occasions, in order to reduce the source magnetic radiation effect | |
Fillers | 40% Glass Fiber | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |