General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.82 g/cm³ Show Supplier Material materials with Density of 1.82 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.02 % Show Supplier Material materials with Water absorption of 0.02 % | ISO 62 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 1.5 % Show Supplier Material materials with Elongation of 1.5 % | ISO 527 |
Flexural modulus | 23.0 °C | 17 GPa Show Supplier Material materials with Flexural modulus of 17 GPa | ISO 178 |
Flexural strength | 23.0 °C | 255 MPa Show Supplier Material materials with Flexural strength of 255 MPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179 |
Tensile strength | 23.0 °C | 160 MPa Show Supplier Material materials with Tensile strength of 160 MPa | ISO 527 |
Thermal
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 175 V Show Supplier Material materials with Comparative tracking index of 175 V | IEC 60112 |
Dielectric constant | 23.0 °C | 5 [-] Show Supplier Material materials with Dielectric constant of 5 [-] | IEC 60250 |
Dielectric strength | 23.0 °C | 15 kV/mm Show Supplier Material materials with Dielectric strength of 15 kV/mm | IEC 60243 |
Dissipation factor | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor of 1E-3 [-] | IEC 60250 |
Volume resistivity | 23.0 °C | 1.80E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.80E+15 Ω·cm | IEC 60093 |
Technological properties
Property | ||
---|---|---|
Application areas | Can be used in Automobile generator rectifier bracket, electronic regulator bracket, collector ring, tuner, etc. | |
Fillers | 55% Glass Fiber and Mineral Powder | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |