Property | Value | Comment |
---|---|---|
Density | 1.29 g/cm³ Show Supplier Material materials with Density of 1.29 g/cm³ | ASTM D792 |
Dimension
Property | Value | Comment |
---|---|---|
Diameter | 1.75 mm Show Supplier Material materials with Diameter of 1.75 mm | Tolerance +/- 0.02 mm |
Mechanical
Property | Value | Comment |
---|---|---|
Elastic modulus | 2.98 GPa Show Supplier Material materials with Elastic modulus of 2.98 GPa | ISO 527-2 |
Elongation | 29 % Show Supplier Material materials with Elongation of 29 % | ISO 527-2 |
Flexural modulus | 2.04 GPa Show Supplier Material materials with Flexural modulus of 2.04 GPa | ISO 172 |
Flexural strength | 68 MPa Show Supplier Material materials with Flexural strength of 68 MPa | ISO 172 |
Hardness, Shore A | 76.0 [-] Show Supplier Material materials with Hardness, Shore A of 76.0 [-] | ASTM D2240 |
Tensile strength | 20 MPa Show Supplier Material materials with Tensile strength of 20 MPa | ISO 527-2 |
Yield strength | 51.0 MPa Show Supplier Material materials with Yield strength of 51.0 MPa | ISO 527-2 |
Thermal
Property | Value | Pressure | Comment |
---|---|---|---|
Glass transition temperature | 80.0 °C Show Supplier Material materials with Glass transition temperature of 80.0 °C | ASTM D3418 | |
Heat deflection temperature | 68 °C Show Supplier Material materials with Heat deflection temperature of 68 °C | 0.45 MPa | ISO 75-2 |
Vicat softening temperature | 78.0 °C Show Supplier Material materials with Vicat softening temperature of 78.0 °C | ISO 3076 |
Technological properties
Property | ||
---|---|---|
Application areas | END-USE PARTS: containers, holders - PROTOTYPES: bottles, packaging - ELECTRONICS: covers, cases, products containing diodes - DECORATIONS: lamps, glass-resembling elements - JEWELLERY: rings, necklaces, bracelets | |
Certifications | Food Contact approved | |
Processing methods | Print temperature: 230-250°C, Bed temperature: 90°C |