Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 1.03 g/cm³ Show Supplier Material materials with Density of 1.03 g/cm³ | ASTM D792 |
Dimension
Mechanical
| Property | Value | Comment |
|---|---|---|
Elongation | 30 % Show Supplier Material materials with Elongation of 30 % | ASTM D638 |
Flexural modulus | 2.15 GPa Show Supplier Material materials with Flexural modulus of 2.15 GPa | ASTM D790 |
Flexural strength | 60.81 MPa Show Supplier Material materials with Flexural strength of 60.81 MPa | ASTM D790 |
Yield strength | 37.75 MPa Show Supplier Material materials with Yield strength of 37.75 MPa | ASTM D638 |
Thermal
| Property | Value | Pressure | Comment |
|---|---|---|---|
Heat deflection temperature | 90 °C Show Supplier Material materials with Heat deflection temperature of 90 °C | 1.8 MPa | ASTM D648, unannealed-annealed condition |
95 °C Show Supplier Material materials with Heat deflection temperature of 95 °C | 1.8 MPa | ASTM D648, unannealed-annealed condition | |
Vicat softening temperature | 103.0 °C Show Supplier Material materials with Vicat softening temperature of 103.0 °C | ASTM D1525 |
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Melt mass-flow rate | 1.1 g/10min Show Supplier Material materials with Melt mass-flow rate of 1.1 g/10min | ASTM D1238 , 200°C/5Kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | PROTOTYPES: linking elements, elements which require high temperature resistance - TOOLS OR THEIR ELEMENTS: gears, racks, elements which require high durability - GADGETS OR THEIR PARTS: phone cases, stands, keychains - TOYS: bricks, robots or their parts, car elements - HOUSE EQUIPMENT: hangers, flower pots, vases | |
| Processing methods | Bed heating required, chamber heating is not required but when using we suggest to keep 80°C. Printing temperature: 250-265°C, Bed temperature: 90-110°C | |