Properties
General
| Property | Value |
|---|---|
Density | 9.13 g/cm³ Show Supplier Material materials with Density of 9.13 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20 °C | 225 GPa Show Supplier Material materials with Elastic modulus of 225 GPa | |
250 °C | 214 GPa Show Supplier Material materials with Elastic modulus of 214 GPa | ||
500 °C | 188 GPa Show Supplier Material materials with Elastic modulus of 188 GPa | ||
Elongation | 30 % Show Supplier Material materials with Elongation of 30 % | ||
Tensile strength | 860 MPa Show Supplier Material materials with Tensile strength of 860 MPa | min. |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 0.0000123 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.0000123 1/K | 20 to 100°C |
Melting point | 1330.0 - 1410.0 °C Show Supplier Material materials with Melting point of 1330.0 - 1410.0 °C | |
Thermal conductivity | 9.4 W/(m·K) Show Supplier Material materials with Thermal conductivity of 9.4 W/(m·K) |
Electrical
| Property | Value |
|---|---|
Electrical resistivity | 8.800000000000001e-10 Ω·m Show Supplier Material materials with Electrical resistivity of 8.800000000000001e-10 Ω·m |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Carbon | 0.05 - 0.15 % Show Supplier Material materials with Carbon of 0.05 - 0.15 % | |
Chromium | 19.0 - 21.0 % Show Supplier Material materials with Chromium of 19.0 - 21.0 % | |
Iron | 3.0 Show Supplier Material materials with Iron of 3.0 | max. |
Manganese | 1.0 - 2.0 % Show Supplier Material materials with Manganese of 1.0 - 2.0 % | |
Nickel | 9.0 - 11.0 % Show Supplier Material materials with Nickel of 9.0 - 11.0 % | |
Phosphorus | 0.04 Show Supplier Material materials with Phosphorus of 0.04 | max. |
Silicon | 0.4 Show Supplier Material materials with Silicon of 0.4 | max. |
Sulfur | 0.03 Show Supplier Material materials with Sulfur of 0.03 | max. |
Tungsten | 14.0 - 16.0 % Show Supplier Material materials with Tungsten of 14.0 - 16.0 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | ||
| Corrosion properties | UGI® HT605 has excellent corrosion resistance at the high temperatures found in aircraft engines. Resistance to oxidation is good when maintained intermittently at up to 870°C and continuously at up to 1090°C. This grade is highly-resistant to flaking and oxidation under extreme conditions. | |
| General machinability | HT605 alloy is machinable using conventional techniques. However, we recommend high-speed steel tools (M40 type) or carbide tools (C1, C2 or C3 type) used on rigid equipment. HT605 alloy is more difficult to machine than austenitic stainless steels (302, 304, 321, and 347 types). Generally, we suggest reducing the feed rates, cutting speeds and pass depths. Please contact our technical assistance team for further information. | |
| Other | Available products: Others on demand. | |