General
Property | Value |
---|---|
Density | 7.8 g/cm³ Show Supplier Material materials with Density of 7.8 g/cm³ |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 20 °C | 200 GPa Show Supplier Material materials with Elastic modulus of 200 GPa |
100 °C | 194 GPa Show Supplier Material materials with Elastic modulus of 194 GPa | |
200 °C | 186 GPa Show Supplier Material materials with Elastic modulus of 186 GPa | |
300 °C | 180 GPa Show Supplier Material materials with Elastic modulus of 180 GPa | |
Tensile strength | 620.0 - 880.0 MPa Show Supplier Material materials with Tensile strength of 620.0 - 880.0 MPa |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 0.000013 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.000013 1/K | 20 to 100°C |
0.000014 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.000014 1/K | 20 to 300°C | |
0.000135 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.000135 1/K | 20 to 200°C | |
Specific heat capacity | 500 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 500 J/(kg·K) | |
Thermal conductivity | 16 W/(m·K) Show Supplier Material materials with Thermal conductivity of 16 W/(m·K) |
Electrical
Property | Value |
---|---|
Electrical resistivity | 8e-07 Ω·m Show Supplier Material materials with Electrical resistivity of 8e-07 Ω·m |
Chemical properties
Property | Value | Comment |
---|---|---|
Carbon | 0.03 Show Supplier Material materials with Carbon of 0.03 | max. |
Chromium | 26.0 - 27.0 % Show Supplier Material materials with Chromium of 26.0 - 27.0 % | |
Manganese | 1.0 Show Supplier Material materials with Manganese of 1.0 | max. |
Molybdenum | 1.3 - 1.8 % Show Supplier Material materials with Molybdenum of 1.3 - 1.8 % | |
Nickel | 4.5 - 5.0 % Show Supplier Material materials with Nickel of 4.5 - 5.0 % | |
Nitrogen | 0.05 - 0.2 % Show Supplier Material materials with Nitrogen of 0.05 - 0.2 % | |
Phosphorus | 0.035 Show Supplier Material materials with Phosphorus of 0.035 | max. |
Silicon | 0.75 Show Supplier Material materials with Silicon of 0.75 | max. |
Sulfur | 0.02 - 0.03 % Show Supplier Material materials with Sulfur of 0.02 - 0.03 % |
Technological properties
Property | ||
---|---|---|
Application areas | Hydraulic and pneumatic mechanisms | |
Corrosion properties | As UGICHROM® is "stainless in mass" there are no corrosion resistance problems over time, provided that the chosen grade is appropriate to the place of use. Passive layer: Stainless steels produce a very fine surface film of oxide consisting of chromium oxides and hydroxides a few Angströms thick. This oxide, commonly called a passive layer, protects the stainless steel against external attacks and gives it the property known as inoxidibility which guarantees the corrosion resistance of these alloys. The passive layer is an intrinsic part of the material, unlike the "Nickel-Chromium" coating deposited on carbon steels, which explains why stainless steel exhibits the basic corrosion resistance and adhesion advantages of chromium under harsh mechanical operating conditions (buckling). Once formed, this passive layer is completely stable since its thickness remains constant. The passive layer inhibits any exchange between the metal and the outside: in the event of damage to the material (scratch, cut, impact, drilling, deformation, etc.), it reforms spontaneously. This self-restructuring is also called "Repassivation". Choosing the most suitable grade: Only choosing the grade that is most appropriate to the operating environment increases the durability of hydraulic cylinders, depending on use. The figure on the right side of the material page shows how to obtain the best compromise between mechanical strength and corrosion resistance (see the chart on the right side of the material page). | |
Other | The mechanical properties of UGICHROM® are suitable for all hydraulic applications: Conditioning: The UGICHROM® product range offers a wide variety of conditioning options suitable for all customers' needs: Individual protection: Possibility of continuous ink jet marking on individual extruded plastic protection. Packaging: |