General
Property | Value |
---|---|
Density | 7.7 g/cm³ Show Supplier Material materials with Density of 7.7 g/cm³ |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23 °C | 215 GPa Show Supplier Material materials with Elastic modulus of 215 GPa | |
100 °C | 215 GPa Show Supplier Material materials with Elastic modulus of 215 GPa | ||
Elongation | 15 % Show Supplier Material materials with Elongation of 15 % | ||
Hardness, Brinell | 321.0 Show Supplier Material materials with Hardness, Brinell of 321.0 | max. | |
Reduction of area | 45.0 % Show Supplier Material materials with Reduction of area of 45.0 % | ||
Tensile strength | 795 MPa Show Supplier Material materials with Tensile strength of 795 MPa | min. |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 0.0000105 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.0000105 1/K | 20 to 100°C |
Specific heat capacity | 460 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 460 J/(kg·K) | |
Thermal conductivity | 25 W/(m·K) Show Supplier Material materials with Thermal conductivity of 25 W/(m·K) |
Electrical
Property | Value |
---|---|
Electrical resistivity | 7e-07 Ω·m Show Supplier Material materials with Electrical resistivity of 7e-07 Ω·m |
Chemical properties
Property | Value | Comment |
---|---|---|
Carbon | 0.16 - 0.2 % Show Supplier Material materials with Carbon of 0.16 - 0.2 % | |
Chromium | 15.5 - 17.0 % Show Supplier Material materials with Chromium of 15.5 - 17.0 % | |
Manganese | 1.0 Show Supplier Material materials with Manganese of 1.0 | max. |
Phosphorus | 0.035 Show Supplier Material materials with Phosphorus of 0.035 | max. |
Silicon | 0.8 Show Supplier Material materials with Silicon of 0.8 | max. |
Sulfur | 0.015 - 0.03 % Show Supplier Material materials with Sulfur of 0.015 - 0.03 % |
Technological properties
Property | ||
---|---|---|
Application areas | Process and energy industry, Chemical industry, Oil and petrochemical industries, Household and electrical appliance industry, Automotive and transport industry, Arms industry | |
Corrosion properties | This alloy has excellent atmospheric corrosion resistance and is one of the standard martensitic grades best able to withstand corrosion in marine environments; only structurally hardened grades such as UGIMA® 4542 have a higher re-sistance (amongst martensitic grades). UGIMA® 4057 is also resistant to certain petroleum and organic products. Precautionary measures should be taken for certain tests such as the saline mist test (French standard NFX 41002), for example marking labels (that might cause corrosion run-outs and reduce the test resistance time) should not be used on the test pieces. In terms of pitting corrosion UGIMA® 4057 performs better than most martensiitic grades. | |
Hot forming | Forging: UGIMA® 4057 is suitable for forging. It is heated slowly to 850°C, then more quickly to 1150/1180°C for forging be-tween 1180°C and 950°C. Forging must be followed by a stress relief heat treatment at 200°C or softening at between 750 and 850°C or hardening and tempering | |
Other | Available products: |
Provided certain precautionary measures are taken, UGIMA® 4057 can be subjected to most arc welding or resistance welding techniques in tempered, hardened or softened condition.
To prevent any risk of cold weld cracking, UGIMA® 4057 must be preheated to between 200 and 300°C and the temper-atures between passes maintained at a minimum of 200°C. A stress relief heat treatment at 650°C is also required after welding.
If a filler metal is needed, a wire with a similar composition to that of UGIMA® 4057, such as AWS E/ER410 is recom-mended. AWS E/ER310 austenitic wire can also be used if the mechanical properties on welding and the response of the welding to the post welding heat treatment are not required to be the same as those of the base metal.
Ar + 1 to 3% CO₂ or O₂ shielding gases are recommended for MIG welding. Gas containing H₂ should not be used. Coated electrodes must be oven dried before welding.Heat treatment