General
Property | Value |
---|---|
Density | 7.9 g/cm³ Show Supplier Material materials with Density of 7.9 g/cm³ |
Mechanical
Property | Value |
---|---|
Elastic modulus | 200 GPa Show Supplier Material materials with Elastic modulus of 200 GPa |
Elongation | 56 % Show Supplier Material materials with Elongation of 56 % |
Reduction of area | 72.0 % Show Supplier Material materials with Reduction of area of 72.0 % |
Tensile strength | 560 MPa Show Supplier Material materials with Tensile strength of 560 MPa |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 0.0000168 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.0000168 1/K | 20 to 200°C |
Thermal conductivity | 15 W/(m·K) Show Supplier Material materials with Thermal conductivity of 15 W/(m·K) |
Electrical
Property | Value |
---|---|
Electrical resistivity | 7.4e-07 Ω·m Show Supplier Material materials with Electrical resistivity of 7.4e-07 Ω·m |
Chemical properties
Property | Value | Comment |
---|---|---|
Carbon | 0.05 Show Supplier Material materials with Carbon of 0.05 | max. |
Chromium | 16.5 - 18.5 % Show Supplier Material materials with Chromium of 16.5 - 18.5 % | |
Manganese | 2.0 Show Supplier Material materials with Manganese of 2.0 | max. |
Molybdenum | 2.0 - 2.5 % Show Supplier Material materials with Molybdenum of 2.0 - 2.5 % | |
Nickel | 10.5 - 11.5 % Show Supplier Material materials with Nickel of 10.5 - 11.5 % | |
Phosphorus | 0.045 Show Supplier Material materials with Phosphorus of 0.045 | max. |
Silicon | 1.0 Show Supplier Material materials with Silicon of 1.0 | max. |
Sulfur | 0.015 - 0.03 % Show Supplier Material materials with Sulfur of 0.015 - 0.03 % | |
Titanium | 0.7000000000000001 Show Supplier Material materials with Titanium of 0.7000000000000001 | max., min: 5xC |
Technological properties
Property | ||
---|---|---|
Corrosion properties | UGIMA® 4571 has excellent ability to withstand corrosion. The table below illustrates a performance scale (with three levels: good/average/excellent) in different environments: | |
General machinability | UGIMA® 4571 offers improved machining performance as a result of the optimization of the inclusion population. This expands the range of cutting conditions suited to the production of machined parts. The productivity gains brought by this new grade are derived from extended tool life, good chip breakability and good surface finish. | |
Heat Treatment | The annealing treatment that gives UGIMA® 4571 its lowest properties includes heating to 1020°C - 1120°C, followed by rapid air or water cooling. | |
Hot forming | Forging: | |
Other | Available products: Do not hesitate to contact the supplier for further information | |
Welding | UGIMA® 4571 can be MIG or TIG welded, with or without filler material, using laser or resistance welding techniques. When using filler wire, we recommend using ER318 (Nb stabilised). For cold applications, ER316LSi wire can also be used. To minimize thermal cracking problems, tight control over welding parameters is required. To do this, always ensure when using arc welding that the linear welding power is limited. |