UGI® 4114 Drawn Bar

Want to keep this datasheet? Save it now in your required format

Description

Resulphurized ferritic stainless steel with molybdenum, with pitting corrosion resistance similar to that of UGIMA®4305 depending on environments and with good machinability and good ferromagnetic properties.

Ferritic supplied in the annealed (softened) condition: micro structure composed of ferrite, chromium carbides and MnS inclusions.

Related Standards

Equivalent Materials

This material data has been provided by Ugitech SA.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

23.0 °C

7.8 g/cm³

Show Supplier Material materials with Density of 7.8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

220 GPa

Show Supplier Material materials with Elastic modulus of 220 GPa

Elongation

23.0 °C

10 %

Show Supplier Material materials with Elongation of 10 %

min.

Tensile strength

23.0 °C

550 - 800 MPa

Show Supplier Material materials with Tensile strength of 550 - 800 MPa

Yield strength Rp0.2

23.0 °C

500 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 500 MPa

min.

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

100.0 °C

1.11E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.11E-5 1/K

for 20 to mentioned temperature

Thermal conductivity

23.0 °C

15 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 15 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical resistivity

23.0 °C

6.1E-7 Ω·m

Show Supplier Material materials with Electrical resistivity of 6.1E-7 Ω·m

Magnetic

PropertyTemperatureValueComment

Coercive force

23.0 °C

300 - 400 A/m

Show Supplier Material materials with Coercive force of 300 - 400 A/m

Drawn bar with magnetic annealing and >600 only drawn.

Relative magnetic permeability

23.0 °C

900 - 1100 [-]

Show Supplier Material materials with Relative magnetic permeability of 900 - 1100 [-]

Drawn bar with magnetic annealing and <500 only drawn.

Remanence

23.0 °C

0.8 - 1 T

Show Supplier Material materials with Remanence of 0.8 - 1 T

Drawn bar with magnetic annealing and 0.6-0.8 only drawn.

Saturation polarization

23.0 °C

1.57 T

Show Supplier Material materials with Saturation polarization of 1.57 T

Drawn bar with magnetic annealing

Chemical properties

PropertyValueComment

Carbon

0.08 %

Show Supplier Material materials with Carbon of 0.08 %

max.

Chromium

17.5 - 18.5 %

Show Supplier Material materials with Chromium of 17.5 - 18.5 %

Iron

Balance

Manganese

1 %

Show Supplier Material materials with Manganese of 1 %

max.

Molybdenum

1.5 - 2.5 %

Show Supplier Material materials with Molybdenum of 1.5 - 2.5 %

Nitrogen

0.07 %

Show Supplier Material materials with Nitrogen of 0.07 %

max.

Phosphorus

0.04 %

Show Supplier Material materials with Phosphorus of 0.04 %

max.

Silicon

1 %

Show Supplier Material materials with Silicon of 1 %

max.

Sulfur

0.15 - 0.25 %

Show Supplier Material materials with Sulfur of 0.15 - 0.25 %

max.

Technological properties

Property
Application areas

  • Building (screws, bolts, etc., door handles)
  • Food processing (solenoid valve)
  • Process: solenoid valves
  • Automotive: miscellaneous parts, sensors, etc.

  • Corrosion properties

    Generalized corrosion in 2M sulphuric acid and at ambient temperature. Good resistance to generalized corrosion in sulphuric acid, better than that of UGI®4105.


    Pitting corrosion in a 0.02M NaCl environment, neutral pH and at ambient temperature. Similar to that of UGIMA® 4305 and UGIMA® 4307HM.


    Crevice corrosion in a 2M NaCl environment and at ambient temperature. Better than that of UGIMA® 4305 or UGI® 4105.


    Neutral salt spray corrosion (5% NaCl 35°C) - ASTM standard B117. Better than that of UGIMA® 4305 or UGI®4105, similar to that of UGIMA® 4307HM.

    General machinability

    Turning: UGI® 4114 has very good turning machinability (better than that of UGI® 4305).


    Drilling: UGI® 4114 has very good drilling machinability, although slightly lower than that of UGI®4305 or UGI®4105


    Heat Treatment

    Softening: Maximum softening heat treatment with holding temperature of 800°C followed by air cooling. Do not exceed 825°C.

    Hot forming

    Forging: Heated slowly to 850°C, then more quickly to 1100/1130°C. Forging between 1130°C and 750°C.

    Other

    Available products:


    ProductShapeFinishToleranceDimensions (mm)
    BarsRoundDrawn polished, SMQ drawn polished8-9Ø 6.5-31 mm
    Descaled rolledk13Ø 22-130 mm
    Turned Polished (TP)9-11Ø 22-130 mm
    Turned Polished SMQ9-11Ø 22-55 mm
    Groundh6-h9Ø 5-115 mm
    HexagonalDrawn9-103-60 mm


    Contact the supplier for dimensions

    Surface Treatment

    contact the supplier