Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 6.51 g/cm³ Show Material materials with Density of 6.51 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 68 GPa Show Material materials with Elastic modulus of 68 GPa | Typical for Zirconium |
Elongation A50 | 20.0 °C | 25 % Show Material materials with Elongation A50 of 25 % | |
290.0 °C | 30 % Show Material materials with Elongation A50 of 30 % | ||
Elongation A50, transverse | 20.0 °C | 25 % Show Material materials with Elongation A50, transverse of 25 % | |
290.0 °C | 30 % Show Material materials with Elongation A50, transverse of 30 % | ||
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | Typical for Zirconium |
Shear modulus | 23.0 °C | 35 GPa Show Material materials with Shear modulus of 35 GPa | Typical for Zirconium |
Tensile strength | 20.0 °C | 400 MPa Show Material materials with Tensile strength of 400 MPa | |
290.0 °C | 185 MPa Show Material materials with Tensile strength of 185 MPa | ||
Tensile strength, transverse | 20.0 °C | 385 MPa Show Material materials with Tensile strength, transverse of 385 MPa | |
290.0 °C | 180 MPa Show Material materials with Tensile strength, transverse of 180 MPa | ||
Yield strength Rp0.2 | 20.0 °C | 240 MPa Show Material materials with Yield strength Rp0.2 of 240 MPa | |
290.0 °C | 100 MPa Show Material materials with Yield strength Rp0.2 of 100 MPa | ||
Yield strength Rp0.2, transverse | 20.0 °C | 300 MPa Show Material materials with Yield strength Rp0.2, transverse of 300 MPa | |
290.0 °C | 120 MPa Show Material materials with Yield strength Rp0.2, transverse of 120 MPa | ||
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 5.7E-6 - 7E-6 1/K Show Material materials with Coefficient of thermal expansion of 5.7E-6 - 7E-6 1/K | Typical for Zirconium |
Melting point | 1845 °C Show Material materials with Melting point of 1845 °C | Typical for Zirconium | |
Specific heat capacity | 23.0 °C | 281 - 289 J/(kg·K) Show Material materials with Specific heat capacity of 281 - 289 J/(kg·K) | Typical for Zirconium |
Thermal conductivity | 23.0 °C | 19 - 27 W/(m·K) Show Material materials with Thermal conductivity of 19 - 27 W/(m·K) | Typical for Zirconium |
Chemical properties
| Property | Value |
|---|---|
Chromium | 0.05 - 0.15 % Show Material materials with Chromium of 0.05 - 0.15 % |
Iron | 0.07 - 0.2 % Show Material materials with Iron of 0.07 - 0.2 % |
Nickel | 0.03 - 0.08 % Show Material materials with Nickel of 0.03 - 0.08 % |
Zinc | 1.2 - 1.7 % Show Material materials with Zinc of 1.2 - 1.7 % |