Allgemein
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Dichte | 1.46 g/cm³ Show Supplier Material materials with Dichte of 1.46 g/cm³ | dry | ISO 1183 | |
Moisture absorption | 2 % Show Supplier Material materials with Moisture absorption of 2 % | dry | Sim. to ISO 62 | |
Wasserabsorption | 0.2 % Show Supplier Material materials with Wasserabsorption of 0.2 % | dry | ISO 62 | at 23°C after 24h |
4.8 % Show Supplier Material materials with Wasserabsorption of 4.8 % | dry | Sim. to ISO 62 |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Biegemodul | 10.5 GPa Show Supplier Material materials with Biegemodul of 10.5 GPa | dry, conditioned | ISO 178 | |||
80 °C | 9.8 GPa Show Supplier Material materials with Biegemodul of 9.8 GPa | conditioned | ISO 178 | |||
80 °C | 10 GPa Show Supplier Material materials with Biegemodul of 10 GPa | dry | ISO 178 | |||
120 °C | 9.5 GPa Show Supplier Material materials with Biegemodul of 9.5 GPa | dry | ISO 178 | |||
160 °C | 5.7 GPa Show Supplier Material materials with Biegemodul of 5.7 GPa | dry | ISO 178 | |||
200 °C | 3.9 GPa Show Supplier Material materials with Biegemodul of 3.9 GPa | dry | ISO 178 | |||
Dehnung | -40 °C | 2.8 % Show Supplier Material materials with Dehnung of 2.8 % | dry | ISO 527-1/-2 | ||
2.5 % Show Supplier Material materials with Dehnung of 2.5 % | conditioned | ISO 527-1/-2 | ||||
2.7 % Show Supplier Material materials with Dehnung of 2.7 % | dry | ISO 527-1/-2 | ||||
2.7 % Show Supplier Material materials with Dehnung of 2.7 % | conditioned | ISO 527-1/-2 | ||||
3 % Show Supplier Material materials with Dehnung of 3 % | dry | ISO 527-1/-2 | 1 mm | |||
40 °C | 2.6 % Show Supplier Material materials with Dehnung of 2.6 % | dry | ISO 527-1/-2 | |||
80 °C | 2.8 % Show Supplier Material materials with Dehnung of 2.8 % | dry | ISO 527-1/-2 | |||
80 °C | 3 % Show Supplier Material materials with Dehnung of 3 % | conditioned | ISO 527-1/-2 | |||
100 °C | 2.7 % Show Supplier Material materials with Dehnung of 2.7 % | dry | ISO 527-1/-2 | |||
120 °C | 3 % Show Supplier Material materials with Dehnung of 3 % | dry | ISO 527-1/-2 | |||
160 °C | 5 % Show Supplier Material materials with Dehnung of 5 % | dry | ISO 527-1/-2 | |||
200 °C | 6 % Show Supplier Material materials with Dehnung of 6 % | dry | ISO 527-1/-2 | |||
Elastizitätsmodul | -40 °C | 11.7 GPa Show Supplier Material materials with Elastizitätsmodul of 11.7 GPa | dry | ISO 527-1/-2 | ||
10.5 GPa Show Supplier Material materials with Elastizitätsmodul of 10.5 GPa | conditioned | ISO 527-1/-2 | ||||
11 GPa Show Supplier Material materials with Elastizitätsmodul of 11 GPa | dry, conditioned | ISO 527-1/-2 | ||||
11 GPa Show Supplier Material materials with Elastizitätsmodul of 11 GPa | dry | ISO 527-1/-2 | 1 mm | |||
40 °C | 10.5 GPa Show Supplier Material materials with Elastizitätsmodul of 10.5 GPa | dry | ISO 527-1/-2 | |||
80 °C | 9.5 GPa Show Supplier Material materials with Elastizitätsmodul of 9.5 GPa | conditioned | ISO 527-1/-2 | |||
80 °C | 10.3 GPa Show Supplier Material materials with Elastizitätsmodul of 10.3 GPa | dry | ISO 527-1/-2 | |||
100 °C | 10.2 GPa Show Supplier Material materials with Elastizitätsmodul of 10.2 GPa | dry | ISO 527-1/-2 | |||
120 °C | 9.5 GPa Show Supplier Material materials with Elastizitätsmodul of 9.5 GPa | dry | ISO 527-1/-2 | |||
160 °C | 6 GPa Show Supplier Material materials with Elastizitätsmodul of 6 GPa | dry | ISO 527-1/-2 | |||
200 °C | 4 GPa Show Supplier Material materials with Elastizitätsmodul of 4 GPa | dry | ISO 527-1/-2 | |||
Flexural yield strength | 275 MPa Show Supplier Material materials with Flexural yield strength of 275 MPa | conditioned | ISO 178 | |||
300 MPa Show Supplier Material materials with Flexural yield strength of 300 MPa | dry | ISO 178 | ||||
80 °C | 190 MPa Show Supplier Material materials with Flexural yield strength of 190 MPa | conditioned | ISO 178 | |||
80 °C | 270 MPa Show Supplier Material materials with Flexural yield strength of 270 MPa | dry | ISO 178 | |||
120 °C | 220 MPa Show Supplier Material materials with Flexural yield strength of 220 MPa | dry | ISO 178 | |||
160 °C | 140 MPa Show Supplier Material materials with Flexural yield strength of 140 MPa | dry | ISO 178 | |||
200 °C | 110 MPa Show Supplier Material materials with Flexural yield strength of 110 MPa | dry | ISO 178 | |||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 8 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | conditioned | ISO 179/1eA | ||
-30 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | dry | ISO 179/1eA | |||
23 °C | 8 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | conditioned | ISO 179/1eA | |||
23 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | dry | ISO 179/1eA | |||
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 55.0 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 55.0 kJ/m² | conditioned | ISO 179/1eU | ||
-30 °C | 65 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 65 kJ/m² | dry | ISO 179/1eU | |||
23 °C | 60 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 60 kJ/m² | conditioned | ISO 179/1eU | |||
23 °C | 70 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 70 kJ/m² | dry | ISO 179/1eU | |||
Zugfestigkeit | -40 °C | 240 MPa Show Supplier Material materials with Zugfestigkeit of 240 MPa | dry | ISO 527-1/-2 | ||
190 MPa Show Supplier Material materials with Zugfestigkeit of 190 MPa | conditioned | ISO 527-1/-2 | ||||
195 MPa Show Supplier Material materials with Zugfestigkeit of 195 MPa | conditioned | ISO 527-1/-2 | at low thickness | |||
210 MPa Show Supplier Material materials with Zugfestigkeit of 210 MPa | dry | ISO 527-1/-2 | ||||
220 MPa Show Supplier Material materials with Zugfestigkeit of 220 MPa | dry | ISO 527-1/-2 | 1 mm | at low thickness | ||
40 °C | 200 MPa Show Supplier Material materials with Zugfestigkeit of 200 MPa | dry | ISO 527-1/-2 | |||
80 °C | 120 MPa Show Supplier Material materials with Zugfestigkeit of 120 MPa | conditioned | ISO 527-1/-2 | |||
80 °C | 180 MPa Show Supplier Material materials with Zugfestigkeit of 180 MPa | dry | ISO 527-1/-2 | |||
100 °C | 170 MPa Show Supplier Material materials with Zugfestigkeit of 170 MPa | dry | ISO 527-1/-2 | |||
120 °C | 150 MPa Show Supplier Material materials with Zugfestigkeit of 150 MPa | dry | ISO 527-1/-2 | |||
160 °C | 100 MPa Show Supplier Material materials with Zugfestigkeit of 100 MPa | dry | ISO 527-1/-2 | |||
200 °C | 75 MPa Show Supplier Material materials with Zugfestigkeit of 75 MPa | dry | ISO 527-1/-2 |
Thermisch
Property | Value | Condition | Testing Standard | Pressure | Comment |
---|---|---|---|---|---|
Glasübergangstemperatur | 150 °C Show Supplier Material materials with Glasübergangstemperatur of 150 °C | dry | ISO 11357-1/-2 | 10°C/min | |
160 °C Show Supplier Material materials with Glasübergangstemperatur of 160 °C | dry | ASTM D5026/D7028 | DMTA (tan d) | ||
Koeffizient der thermischen Ausdehnung | 1.8e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.8e-07 1/K | dry | ISO 11359-1/-2 | Parallel | |
6e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6e-07 1/K | dry | ISO 11359-1/-2 | Normal | ||
Schmelzpunkt | 340 °C Show Supplier Material materials with Schmelzpunkt of 340 °C | dry | ISO 11357-1/-3 | 10°C/min | |
Wärmeformbeständigkeitstemperatur | 320 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 320 °C | dry | ISO 75-1/-2 | 2 MPa | |
335 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 335 °C | dry | ISO 75-1/-2 | 0.45 MPa |
Elektrisch
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Dielektrizitätskonstante | 3.83 [-] Show Supplier Material materials with Dielektrizitätskonstante of 3.83 [-] | dry | IEC 60250 | 10GHz |
3.85 [-] Show Supplier Material materials with Dielektrizitätskonstante of 3.85 [-] | dry | IEC 60250 | 5GHz | |
3.88 [-] Show Supplier Material materials with Dielektrizitätskonstante of 3.88 [-] | conditioned | IEC 60250 | 1GHz | |
3.92 [-] Show Supplier Material materials with Dielektrizitätskonstante of 3.92 [-] | dry | IEC 60250 | 1GHz | |
Durchschlagfestigkeit | 40 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 40 kV/mm | conditioned | IEC 60243-1 | |
45 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 45 kV/mm | dry | IEC 60243-1 | ||
Kriechstromfestigkeit | 600 V Show Supplier Material materials with Kriechstromfestigkeit of 600 V | dry | IEC 60112 | |
Surface resistivity | 1e+15 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+15 Ω/sq | conditioned | IEC 62631-3-2 | |
Verlustfaktor | 120 [-] Show Supplier Material materials with Verlustfaktor of 120 [-] | dry | IEC 60250 | 10GHz |
140 [-] Show Supplier Material materials with Verlustfaktor of 140 [-] | dry | IEC 60250 | 5GHz | |
170 [-] Show Supplier Material materials with Verlustfaktor of 170 [-] | dry, conditioned | IEC 60250 | 1GHz | |
Volume resistivity | 1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry, conditioned | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber |