General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 2.65 g/cm³ Show Material materials with Density of 2.65 g/cm³ | F | EN 1706, EN 13195 | Casting | |
20.0 °C | 2.65 g/cm³ Show Material materials with Density of 2.65 g/cm³ | F | EN 1706 |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 - 90.0 MPa Show Material materials with Bending Fatigue Strength of 60.0 - 90.0 MPa | F | EN 1706, EN 13195 | Casting | ||
Elastic modulus | 75.0 GPa Show Material materials with Elastic modulus of 75.0 GPa | F | EN 1706, EN 13195 | Casting | ||
20.0 °C | 75.0 GPa Show Material materials with Elastic modulus of 75.0 GPa | F | EN 1706 | |||
Hardness, Brinell | 45.0 [-] Show Material materials with Hardness, Brinell of 45.0 [-] | F | EN 1706, EN 13195 | Casting | ||
20.0 °C | 45.0 [-] Show Material materials with Hardness, Brinell of 45.0 [-] | F | EN 1706 | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Cast 4xx.x Series Aluminium | ||||
Tensile strength | 150.0 MPa Show Material materials with Tensile strength of 150.0 MPa | F | EN 1706, EN 13195 | Casting | ||
170.0 MPa Show Material materials with Tensile strength of 170.0 MPa | F | EN 1706, EN 13195 | Casting | |||
20.0 °C | 150.0 MPa Show Material materials with Tensile strength of 150.0 MPa | F | EN 1706 | |||
20.0 °C | 170.0 MPa Show Material materials with Tensile strength of 170.0 MPa | F | EN 1706 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.1e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 1/K | F | EN 1706, EN 13195 | Casting |
100.0 °C | 2.1e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 1/K | F | EN 1706, EN 13195 | Casting | |
100 °C | 2.1e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 1/K | F | EN 1706, EN 13195 | Casting | |
Melting point | 570.0 - 590.0 °C Show Material materials with Melting point of 570.0 - 590.0 °C | F | EN 1706, EN 13195 | Casting | |
Specific heat capacity | 910.0 J/(kg·K) Show Material materials with Specific heat capacity of 910.0 J/(kg·K) | F | EN 1706, EN 13195 | Casting | |
20.0 °C | 910.0 J/(kg·K) Show Material materials with Specific heat capacity of 910.0 J/(kg·K) | F | EN 1706 | ||
Thermal conductivity | 20.0 °C | 140.0 - 170.0 W/(m·K) Show Material materials with Thermal conductivity of 140.0 - 170.0 W/(m·K) | F | EN 1706, EN 13195 | Casting |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 18000000.0 - 24000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 24000000.0 S/m | F | EN 1706, EN 13195 | Casting |
Electrical resistivity | 4.17e-08 - 5.56e-08 Ω·m Show Material materials with Electrical resistivity of 4.17e-08 - 5.56e-08 Ω·m | F | EN 1706, EN 13195 | Casting |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 87.09 % Show Material materials with Aluminium of 87.09 % | F | EN 1706 | |
Copper | 0.05 % Show Material materials with Copper of 0.05 % | F | EN 1706, EN 13195 | Casting |
Iron | 0.19 % Show Material materials with Iron of 0.19 % | F | EN 1706 | |
0.19 % Show Material materials with Iron of 0.19 % | F | EN 1706, EN 13195 | Casting | |
Magnesium | 0.45 % Show Material materials with Magnesium of 0.45 % | F | EN 1706, EN 13195 | Casting |
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % | F | EN 1706, EN 13195 | Casting |
Silicon | 10.0 - 11.8 % Show Material materials with Silicon of 10.0 - 11.8 % | F | EN 1706, EN 13195 | Casting |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | F | EN 1706, EN 13195 | Casting |
Zinc | 0.07 % Show Material materials with Zinc of 0.07 % | F | EN 1706, EN 13195 | Casting |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: not recommended | |
Corrosion properties | general: good | |
General machinability | after thermal treatment: acceptable | |
Processing methods | permanent mould casting, separately cast test sample |