Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 2.65 g/cm³ Show Material materials with Density of 2.65 g/cm³ | F | EN 1706 | Casting | |
20.0 °C | 2.65 g/cm³ Show Material materials with Density of 2.65 g/cm³ | F | EN 1706 |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 - 90.0 MPa Show Material materials with Bending Fatigue Strength of 60.0 - 90.0 MPa | F | EN 1706 | Casting | ||
Elastic modulus | 75.0 GPa Show Material materials with Elastic modulus of 75.0 GPa | F | EN 1706 | Casting | ||
20.0 °C | 75.0 GPa Show Material materials with Elastic modulus of 75.0 GPa | F | EN 1706 | |||
Hardness, Brinell | 60.0 [-] Show Material materials with Hardness, Brinell of 60.0 [-] | F | EN 1706 | Casting | ||
20.0 °C | 60.0 [-] Show Material materials with Hardness, Brinell of 60.0 [-] | F | EN 1706 | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Cast 4xx.x Series Aluminium | ||||
Tensile strength | 240.0 MPa Show Material materials with Tensile strength of 240.0 MPa | F | EN 1706 | Casting | ||
20.0 °C | 240.0 MPa Show Material materials with Tensile strength of 240.0 MPa | F | EN 1706 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 1.9999999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.9999999999999998e-05 1/K | F | EN 1706 | Casting |
20 °C | 2.1e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 1/K | F | EN 1706 | Casting | |
100 °C | 1.9999999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.9999999999999998e-05 1/K | F | EN 1706 | Casting | |
100.0 °C | 2e-05 1/K Show Material materials with Coefficient of thermal expansion of 2e-05 1/K | F | EN 1706 | ||
200 °C | 2.1e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 1/K | F | EN 1706 | Casting | |
Melting point | 570.0 - 580.0 °C Show Material materials with Melting point of 570.0 - 580.0 °C | F | EN 1706 | Casting | |
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | F | EN 1706 | Casting | |
20.0 °C | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | F | EN 1706 | ||
Thermal conductivity | 20.0 °C | 130.0 - 160.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 - 160.0 W/(m·K) | F | EN 1706 | Casting |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 16000000.0 - 22000000.0 S/m Show Material materials with Electrical conductivity of 16000000.0 - 22000000.0 S/m | F | EN 1706 | Casting |
Electrical resistivity | 4.55e-08 - 6.25e-08 Ω·m Show Material materials with Electrical resistivity of 4.55e-08 - 6.25e-08 Ω·m | F | EN 1706 | Casting |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 84.3 % Show Material materials with Aluminium of 84.3 % | F | EN 1706 | |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | F | EN 1706 | Casting |
Iron | 1.0 % Show Material materials with Iron of 1.0 % | F | EN 1706 | |
1.00 % Show Material materials with Iron of 1.00 % | F | EN 1706 | Casting | |
Manganese | 0.55 % Show Material materials with Manganese of 0.55 % | F | EN 1706 | Casting |
Silicon | 10.5 - 13.5 % Show Material materials with Silicon of 10.5 - 13.5 % | F | EN 1706 | Casting |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | F | EN 1706 | Casting |
Zinc | 0.15 % Show Material materials with Zinc of 0.15 % | F | EN 1706 | Casting |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: not recommended | |
Corrosion properties | general: acceptable | |
General machinability | after thermal treatment: acceptable | |
Processing methods | pressure die casting, separately cast test sample |