General
Property | Value | Comment |
---|---|---|
Density | 2.65 - 2.7 g/cm³ Show Material materials with Density of 2.65 - 2.7 g/cm³ | Typical for Cast 3xx.x Series Aluminium |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Bending Fatigue Strength | 70.0 - 100.0 MPa Show Material materials with Bending Fatigue Strength of 70.0 - 100.0 MPa | T6 | EN 1706 | Casting | ||
Elastic modulus | 73.0 - 80.0 GPa Show Material materials with Elastic modulus of 73.0 - 80.0 GPa | Typical for Cast 3xx.x Series Aluminium | ||||
Hardness, Brinell | 100.0 [-] Show Material materials with Hardness, Brinell of 100.0 [-] | T6 | EN 1706 | Casting | ||
110.0 [-] Show Material materials with Hardness, Brinell of 110.0 [-] | T6 | EN 1706 | Casting | |||
20.0 °C | 100.0 [-] Show Material materials with Hardness, Brinell of 100.0 [-] | T6 | EN 1706 | |||
20.0 °C | 110.0 [-] Show Material materials with Hardness, Brinell of 110.0 [-] | T6 | EN 1706 | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | ||||
Shear modulus | 2.8 GPa Show Material materials with Shear modulus of 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | ||||
Tensile strength | 230.0 MPa Show Material materials with Tensile strength of 230.0 MPa | T6 | EN 1706 | Casting | ||
280.0 MPa Show Material materials with Tensile strength of 280.0 MPa | T6 | EN 1706 | Casting | |||
20.0 °C | 230.0 MPa Show Material materials with Tensile strength of 230.0 MPa | T6 | EN 1706 | |||
20.0 °C | 280.0 MPa Show Material materials with Tensile strength of 280.0 MPa | T6 | EN 1706 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.2e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.2e-05 1/K | T6 | EN 1706 | Casting | |
100.0 °C | 2.2e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.2e-05 1/K | T6 | EN 1706 | Casting | ||
100 °C | 2.2e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.2e-05 1/K | T6 | EN 1706 | Casting | ||
Melting point | 505.0 - 770.0 °C Show Material materials with Melting point of 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium | ||||
Specific heat capacity | 960.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 960.0 - 963.0 J/(kg·K) | Typical for Cast 3xx.x Series Aluminium | ||||
Thermal conductivity | 20.0 °C | 140.0 - 150.0 W/(m·K) Show Material materials with Thermal conductivity of 140.0 - 150.0 W/(m·K) | T6 | EN 1706 | Casting |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 19000000.0 - 23000000.0 S/m Show Material materials with Electrical conductivity of 19000000.0 - 23000000.0 S/m | T6 | EN 1706 | Casting |
Electrical resistivity | 4.35e-08 - 5.26e-08 Ω·m Show Material materials with Electrical resistivity of 4.35e-08 - 5.26e-08 Ω·m | T6 | EN 1706 | Casting |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 90.15 % Show Material materials with Aluminium of 90.15 % | T6 | EN 1706 | |
Copper | 1.0 - 1.5 % Show Material materials with Copper of 1.0 - 1.5 % | T6 | EN 1706 | Casting |
Iron | 0.65 % Show Material materials with Iron of 0.65 % | T6 | EN 1706 | |
0.65 % Show Material materials with Iron of 0.65 % | T6 | EN 1706 | Casting | |
Lead | 0.15 % Show Material materials with Lead of 0.15 % | T6 | EN 1706 | Casting |
Magnesium | 0.35 - 0.65 % Show Material materials with Magnesium of 0.35 - 0.65 % | T6 | EN 1706 | Casting |
Manganese | 0.55 % Show Material materials with Manganese of 0.55 % | T6 | EN 1706 | Casting |
Nickel | 0.25 % Show Material materials with Nickel of 0.25 % | T6 | EN 1706 | Casting |
Silicon | 4.5 - 5.5 % Show Material materials with Silicon of 4.5 - 5.5 % | T6 | EN 1706 | Casting |
Tin | 0.05 % Show Material materials with Tin of 0.05 % | T6 | EN 1706 | Casting |
Titanium | 0.05 - 0.25 % Show Material materials with Titanium of 0.05 - 0.25 % | T6 | EN 1706 | Casting |
Zinc | 0.15 % Show Material materials with Zinc of 0.15 % | T6 | EN 1706 | Casting |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: not sufficient | |
Corrosion properties | general: not sufficient | |
General machinability | after thermal treatment: good, as cast: good | |
Processing methods | permanent mould casting, separately cast test sample |