General
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Density | 2.65 g/cm³ Show Material materials with Density of 2.65 g/cm³ | F | EN 1706 | |
20.0 °C | 2.65 g/cm³ Show Material materials with Density of 2.65 g/cm³ | F | DIN 1725-2, EN 1676, EN 1706 |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 - 90.0 MPa Show Material materials with Bending Fatigue Strength of 60.0 - 90.0 MPa | F | EN 1706 | ||
Elastic modulus | 76.0 GPa Show Material materials with Elastic modulus of 76.0 GPa | F | EN 1706 | ||
20.0 °C | 76.0 GPa Show Material materials with Elastic modulus of 76.0 GPa | F | DIN 1725-2, EN 1676, EN 1706 | ||
Elongation | 1.0 % Show Material materials with Elongation of 1.0 % | F | EN 1706 | A50 | |
20.0 °C | 1.0 - 3.0 % Show Material materials with Elongation of 1.0 - 3.0 % | F | DIN 1725-2, EN 1676, EN 1706 | ||
Hardness, Brinell | 70.0 [-] Show Material materials with Hardness, Brinell of 70.0 [-] | F | EN 1706 | ||
20.0 °C | 60.0 - 100.0 [-] Show Material materials with Hardness, Brinell of 60.0 - 100.0 [-] | F | DIN 1725-2, EN 1676, EN 1706 | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | |||
Shear modulus | 2.8 GPa Show Material materials with Shear modulus of 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | |||
Tensile strength | 240.0 MPa Show Material materials with Tensile strength of 240.0 MPa | F | EN 1706 | ||
20.0 °C | 220.0 - 300.0 MPa Show Material materials with Tensile strength of 220.0 - 300.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 |
Thermal
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 1.9999999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.9999999999999998e-05 1/K | F | EN 1706 |
20 °C | 2.1e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 1/K | F | DIN 1725-2, EN 1676, EN 1706 | |
100 °C | 1.9999999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.9999999999999998e-05 1/K | F | EN 1706 | |
200.0 °C | 2.1e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 1/K | F | DIN 1725-2, EN 1676, EN 1706 | |
200 °C | 2.1e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 1/K | F | DIN 1725-2, EN 1676, EN 1706 | |
Melting point | 530.0 - 580.0 °C Show Material materials with Melting point of 530.0 - 580.0 °C | F | EN 1706 | |
Specific heat capacity | 890.0 J/(kg·K) Show Material materials with Specific heat capacity of 890.0 J/(kg·K) | F | EN 1706 | |
20.0 °C | 890.0 J/(kg·K) Show Material materials with Specific heat capacity of 890.0 J/(kg·K) | F | DIN 1725-2, EN 1676, EN 1706 | |
Thermal conductivity | 120.0 - 150.0 W/(m·K) Show Material materials with Thermal conductivity of 120.0 - 150.0 W/(m·K) | F | EN 1706 | |
20.0 °C | 120.0 - 140.0 W/(m·K) Show Material materials with Thermal conductivity of 120.0 - 140.0 W/(m·K) | F | DIN 1725-2, EN 1676, EN 1706 |
Electrical
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Electrical conductivity | 15000000.0 - 20000000.0 S/m Show Material materials with Electrical conductivity of 15000000.0 - 20000000.0 S/m | F | EN 1706 | |
20.0 °C | 16000000.0 - 20000000.0 S/m Show Material materials with Electrical conductivity of 16000000.0 - 20000000.0 S/m | F | DIN 1725-2, EN 1676, EN 1706 | |
Electrical resistivity | 5e-08 - 6.67e-08 Ω·m Show Material materials with Electrical resistivity of 5e-08 - 6.67e-08 Ω·m | F | EN 1706 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 81.9 % Show Material materials with Aluminium of 81.9 % | F | DIN 1725-2, EN 1676, EN 1706 |
Copper | 1.2 % Show Material materials with Copper of 1.2 % | F | DIN 1725-2, EN 1676, EN 1706 |
Iron | 1.2 % Show Material materials with Iron of 1.2 % | F | DIN 1725-2, EN 1676, EN 1706 |
1.20 % Show Material materials with Iron of 1.20 % | F | EN 1706 | |
Lead | 0.2 % Show Material materials with Lead of 0.2 % | F | DIN 1725-2, EN 1676, EN 1706 |
Magnesium | 0.4 % Show Material materials with Magnesium of 0.4 % | F | DIN 1725-2, EN 1676, EN 1706 |
Manganese | 0.1 - 0.5 % Show Material materials with Manganese of 0.1 - 0.5 % | F | DIN 1725-2, EN 1676, EN 1706 |
Nickel | 0.2 % Show Material materials with Nickel of 0.2 % | F | DIN 1725-2, EN 1676, EN 1706 |
Silicon | 10.5 - 13.5 % Show Material materials with Silicon of 10.5 - 13.5 % | F | DIN 1725-2, EN 1676, EN 1706 |
Tin | 0.1 % Show Material materials with Tin of 0.1 % | F | DIN 1725-2, EN 1676, EN 1706 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | F | DIN 1725-2, EN 1676, EN 1706 |
Zinc | 0.5 % Show Material materials with Zinc of 0.5 % | F | DIN 1725-2, EN 1676, EN 1706 |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: not recommended | |
Corrosion properties | general: acceptable | |
General machinability | after thermal treatment: acceptable | |
Processing methods | pressure die casting, separately cast test sample |