Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.26 g/cm³ Show Supplier Material materials with Density of 8.26 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 131 GPa Show Supplier Material materials with Elastic modulus of 131 GPa | |
Elongation A5 | 23.0 °C | 4 % Show Supplier Material materials with Elongation A5 of 4 % | |
Hardness, HBW | 23.0 °C | 380 [-] Show Supplier Material materials with Hardness, HBW of 380 [-] | HBW 10/3000 |
Hardness, Rockwell C | 23.0 °C | 40 [-] Show Supplier Material materials with Hardness, Rockwell C of 40 [-] | |
Tensile strength | 23.0 °C | 1250 MPa Show Supplier Material materials with Tensile strength of 1250 MPa | |
Yield strength Rp0.5 | 23.0 °C | 1000 MPa Show Supplier Material materials with Yield strength Rp0.5 of 1000 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.75E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.75E-5 1/K |
Specific heat capacity | 23.0 °C | 380 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 380 J/(kg·K) |
Thermal conductivity | 20.0 °C | 106 W/(m·K) Show Supplier Material materials with Thermal conductivity of 106 W/(m·K) |
100.0 °C | 130 W/(m·K) Show Supplier Material materials with Thermal conductivity of 130 W/(m·K) | |
200.0 °C | 145 W/(m·K) Show Supplier Material materials with Thermal conductivity of 145 W/(m·K) | |
300.0 °C | 157 W/(m·K) Show Supplier Material materials with Thermal conductivity of 157 W/(m·K) | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 23.0 °C | 1.28E+7 S/m Show Supplier Material materials with Electrical conductivity of 1.28E+7 S/m |
Specific Electrical conductivity | 22 % IACS Show Supplier Material materials with Specific Electrical conductivity of 22 % IACS |
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Beryllium | 1.9 % Show Supplier Material materials with Beryllium of 1.9 % | ||
Cobalt | 0.5 % Show Supplier Material materials with Cobalt of 0.5 % | Co+Ni | |
Copper | Balance | ||
Nickel | 0.5 % Show Supplier Material materials with Nickel of 0.5 % | Co+Ni | |
Other | 0.5 % Show Supplier Material materials with Other of 0.5 % | ||
Technological properties
| Property | ||
|---|---|---|
| Application areas | 2.1247 is used wherever good wear resistance or high mechanical properties are desired coupled with a good electrical or thermal conductivity, such as: Flash butt welding and butt welding, Parts for electrical components, in the plastic mould industry is sometimes used as chill plates and inserts in the moulds, cooling pins and neck rings or bottom plates for blow moulds of plastic bottles. | |