General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.26 g/cm³ Show Supplier Material materials with Density of 8.26 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 126 GPa Show Supplier Material materials with Elastic modulus of 126 GPa | |
Elongation A5 | 23.0 °C | 2 % Show Supplier Material materials with Elongation A5 of 2 % | |
Hardness, HBW | 23.0 °C | 320 [-] Show Supplier Material materials with Hardness, HBW of 320 [-] | HBW 10/3000 |
Hardness, Rockwell C | 23.0 °C | 33 [-] Show Supplier Material materials with Hardness, Rockwell C of 33 [-] | |
Tensile strength | 23.0 °C | 830 MPa Show Supplier Material materials with Tensile strength of 830 MPa | |
Yield strength Rp0.5 | 23.0 °C | 586 MPa Show Supplier Material materials with Yield strength Rp0.5 of 586 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.75E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.75E-5 1/K |
Specific heat capacity | 23.0 °C | 420 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 420 J/(kg·K) |
Thermal conductivity | 23.0 °C | 106 W/(m·K) Show Supplier Material materials with Thermal conductivity of 106 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 23.0 °C | 1.16E+7 S/m Show Supplier Material materials with Electrical conductivity of 1.16E+7 S/m |
Specific Electrical conductivity | 20 % IACS Show Supplier Material materials with Specific Electrical conductivity of 20 % IACS |
Chemical properties
Technological properties
Property | ||
---|---|---|
Application areas | 2.1247 is used wherever good wear resistance or high mechanical properties are desired coupled with a good electrical or thermal conductivity, such as: Flash butt welding and butt welding, Parts for electrical components, in the plastic mould industry is sometimes used as chill plates and inserts in the moulds, cooling pins and neck rings or bottom plates for blow moulds of plastic bottles. |