Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 7.95 g/cm³ Show Supplier Material materials with Density of 7.95 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Charpy impact energy | 23.0 °C | 41 - 54 J Show Supplier Material materials with Charpy impact energy of 41 - 54 J | |
Compressive strength | 23.0 °C | 862 - 931 MPa Show Supplier Material materials with Compressive strength of 862 - 931 MPa | |
Compressive yield strength, 0.1% | 23.0 °C | 324 MPa Show Supplier Material materials with Compressive yield strength, 0.1% of 324 MPa | |
Elastic modulus | 23.0 °C | 124 GPa Show Supplier Material materials with Elastic modulus of 124 GPa | |
Elongation A5 | 23.0 °C | 35 % Show Supplier Material materials with Elongation A5 of 35 % | |
Hardness, HBW | 23.0 °C | 163 - 187 [-] Show Supplier Material materials with Hardness, HBW of 163 - 187 [-] | HBW 10/3000 |
Hardness, Rockwell B | 23.0 °C | 85 - 91 [-] Show Supplier Material materials with Hardness, Rockwell B of 85 - 91 [-] | |
Izod impact energy | 23.0 °C | 61 - 75 J Show Supplier Material materials with Izod impact energy of 61 - 75 J | |
Proportional limit in compression | 23.0 °C | 138 - 179 MPa Show Supplier Material materials with Proportional limit in compression of 138 - 179 MPa | |
Reduction of area | 23.0 °C | 55 - 63 % Show Supplier Material materials with Reduction of area of 55 - 63 % | |
Shear strength | 23.0 °C | 276 - 331 MPa Show Supplier Material materials with Shear strength of 276 - 331 MPa | |
Tensile strength | 23.0 °C | 517 - 586 MPa Show Supplier Material materials with Tensile strength of 517 - 586 MPa | |
Yield strength Rp0.5 | 23.0 °C | 283 - 386 MPa Show Supplier Material materials with Yield strength Rp0.5 of 283 - 386 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.63E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.63E-5 1/K |
Specific heat capacity | 23.0 °C | 420 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 420 J/(kg·K) |
Thermal conductivity | 23.0 °C | 54 W/(m·K) Show Supplier Material materials with Thermal conductivity of 54 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 23.0 °C | 7.00E+6 S/m Show Supplier Material materials with Electrical conductivity of 7.00E+6 S/m |
Specific Electrical conductivity | 12 % IACS Show Supplier Material materials with Specific Electrical conductivity of 12 % IACS |
Chemical properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | AMPCO® 8 is used whenever good resistance to corrosion, erosion, abrasion and cavitation-pitting is essential. AMPCO® 8 is ideally suited for pipes, tubes, joints and other pieces used in the process, marine or other similar industries. The extreme hardness of this alloy makes it an ideal bolting material. AMPCO® 8 has excellent bearing characteristics. It is used for bushings, bearings, wear strips and in similar applications where hardness and ductility are essential for uninterrupted operations. | |