General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 7.95 g/cm³ Show Supplier Material materials with Density of 7.95 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy | 23.0 °C | 54 - 61 J Show Supplier Material materials with Charpy impact energy of 54 - 61 J | |
Compressive strength | 23.0 °C | 689 - 862 MPa Show Supplier Material materials with Compressive strength of 689 - 862 MPa | |
Compressive yield strength, 0.1% | 23.0 °C | 248 MPa Show Supplier Material materials with Compressive yield strength, 0.1% of 248 MPa | |
Elastic modulus | 23.0 °C | 124 GPa Show Supplier Material materials with Elastic modulus of 124 GPa | |
Elongation A5 | 23.0 °C | 40 - 42 % Show Supplier Material materials with Elongation A5 of 40 - 42 % | |
Fatigue strength | 23.0 °C | 145 - 179 MPa Show Supplier Material materials with Fatigue strength of 145 - 179 MPa | 100.000.000 cycles |
Hardness, HBW | 23.0 °C | 140 - 153 [-] Show Supplier Material materials with Hardness, HBW of 140 - 153 [-] | HBW 10/3000 |
Hardness, Rockwell B | 23.0 °C | 78 - 82 [-] Show Supplier Material materials with Hardness, Rockwell B of 78 - 82 [-] | |
Izod impact energy | 23.0 °C | 81 - 88 J Show Supplier Material materials with Izod impact energy of 81 - 88 J | |
Proportional limit in compression | 23.0 °C | 145 - 172 MPa Show Supplier Material materials with Proportional limit in compression of 145 - 172 MPa | |
Reduction of area | 23.0 °C | 35 - 40 % Show Supplier Material materials with Reduction of area of 35 - 40 % | |
Shear strength | 23.0 °C | 290 - 359 MPa Show Supplier Material materials with Shear strength of 290 - 359 MPa | |
Tensile strength | 23.0 °C | 483 - 552 MPa Show Supplier Material materials with Tensile strength of 483 - 552 MPa | |
Yield strength Rp0.5 | 23.0 °C | 214 - 283 MPa Show Supplier Material materials with Yield strength Rp0.5 of 214 - 283 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.63E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.63E-5 1/K |
Specific heat capacity | 23.0 °C | 420 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 420 J/(kg·K) |
Thermal conductivity | 23.0 °C | 54 W/(m·K) Show Supplier Material materials with Thermal conductivity of 54 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 23.0 °C | 7.00E+6 S/m Show Supplier Material materials with Electrical conductivity of 7.00E+6 S/m |
Specific Electrical conductivity | 12 % IACS Show Supplier Material materials with Specific Electrical conductivity of 12 % IACS |
Chemical properties
Technological properties
Property | ||
---|---|---|
Application areas | AMPCO® 8 sheet and plate has excellent corrosion resistance, not only in alkaline or reducing environments but also in oxydising media. This alloy is ideally suited for applications in the chemical and marine industry. Its inherent wear resistance properties make it well adopted for wear strips and wear plates. Other uses, where both corrosion and wear are factors include chutes, troughs and wear plates in contact with both dry and wet abrasive cereals and crystalline chemicals, etc. |