General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 6.93 g/cm³ Show Supplier Material materials with Density of 6.93 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Compressive strength | 23.0 °C | 1551 MPa Show Supplier Material materials with Compressive strength of 1551 MPa | |
Compressive yield strength, 0.1% | 23.0 °C | 689 MPa Show Supplier Material materials with Compressive yield strength, 0.1% of 689 MPa | |
Elastic modulus | 23.0 °C | 110 GPa Show Supplier Material materials with Elastic modulus of 110 GPa | |
Hardness, HBW | 23.0 °C | 375 [-] Show Supplier Material materials with Hardness, HBW of 375 [-] | HBW 10/3000 |
Hardness, Rockwell C | 23.0 °C | 40 [-] Show Supplier Material materials with Hardness, Rockwell C of 40 [-] |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.62E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.62E-5 1/K |
Specific heat capacity | 23.0 °C | 420 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 420 J/(kg·K) |
Thermal conductivity | 23.0 °C | 33 W/(m·K) Show Supplier Material materials with Thermal conductivity of 33 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 23.0 °C | 4.00E+6 S/m Show Supplier Material materials with Electrical conductivity of 4.00E+6 S/m |
Specific Electrical conductivity | 8 % IACS Show Supplier Material materials with Specific Electrical conductivity of 8 % IACS |
Chemical properties
Property | Value |
---|---|
Copper | Balance |
Technological properties
Property | ||
---|---|---|
Application areas | The phenomenal success of this alloy led to its use as forming rolls, bending and wiping blocks and it is considered the standard material in this field of applications. Due to its inherent friction properties, this alloy has an excellent behaviour in any wear application where high compression loads are present. |