General
Property | Temperature | Value | |
---|---|---|---|
Density | 23.0 °C | 15.05 g/cm³ Show Supplier Material materials with Density of 15.05 g/cm³ | |
Grain structure | Ultrafine (0,2µm - 0,5µm) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 646 GPa Show Supplier Material materials with Elastic modulus of 646 GPa | |
Hardness, Rockwell A | 23.0 °C | 94.6 [-] Show Supplier Material materials with Hardness, Rockwell A of 94.6 [-] | |
Hardness, Vickers, 10 | 23.0 °C | 2300 [-] Show Supplier Material materials with Hardness, Vickers, 10 of 2300 [-] | EN ISO 6507-1 |
Hardness, Vickers, 30 | 23.0 °C | 2200 [-] Show Supplier Material materials with Hardness, Vickers, 30 of 2200 [-] | EN ISO 6507-1 |
Plane-Strain Fracture Toughnes | 23.0 °C | 8.4 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 8.4 MPa·√m | ISO 28079 |
Poisson's ratio | 23.0 °C | 0.2 [-] Show Supplier Material materials with Poisson's ratio of 0.2 [-] | |
Tensile strength, transverse | 23.0 °C | 3700 MPa Show Supplier Material materials with Tensile strength, transverse of 3700 MPa | DIN EN ISO 7438 |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 4.62E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 4.62E-6 1/K |
Specific heat capacity | 23.0 °C | 0.19 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 0.19 J/(kg·K) |
Thermal conductivity | 23.0 °C | 59 W/(m·K) Show Supplier Material materials with Thermal conductivity of 59 W/(m·K) |
Thermal diffusivity | 23.0 °C | 21.3 mm²/s Show Supplier Material materials with Thermal diffusivity of 21.3 mm²/s |
Chemical properties
Technological properties
Property |
---|