PE METALEN PE-11K

Alternative and trade names
METALEN PE-11K
Want to keep this datasheet? Save it now in your required format

Description

Composition is based on black HDPE with excellent processability, low shrinkage and temperature stability during processing. In terms of resistance to photooxidative and thermal aging, the composition is close to 273-81K grade, significantly exceeding it in terms of cracking resistance under load.

Related Standards

This material data has been provided by METACLAY .

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValue

Density

23.0 °C

0.9509 g/cm³

Show Supplier Material materials with Density of 0.9509 g/cm³

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

700 %

Show Supplier Material materials with Elongation of 700 %

Flexural modulus

23.0 °C

0.8 GPa

Show Supplier Material materials with Flexural modulus of 0.8 GPa

Min.

Hardness, Shore D

23.0 °C

62 [-]

Show Supplier Material materials with Hardness, Shore D of 62 [-]

Tensile strength

23.0 °C

26 MPa

Show Supplier Material materials with Tensile strength of 26 MPa

Thermal

PropertyValueComment

Brittleness temperature

-70 °C

Show Supplier Material materials with Brittleness temperature of -70 °C

Max.

Electrical

PropertyTemperatureValueComment

Surface insulation resistance

23.0 °C

1.00E+16 Ω·cm²

Show Supplier Material materials with Surface insulation resistance of 1.00E+16 Ω·cm²

Min., GOST 50499

Rheological Properties

PropertyValueComment

Melt mass-flow rate

0.3 - 0.7 g/10min

Show Supplier Material materials with Melt mass-flow rate of 0.3 - 0.7 g/10min

GOST 11645, 190°С/2.16kg

Technological properties

Property
Application areas

METALEN PE-11K is used in the cable manufacture as a jacket of power cables and optical communication cables.

Processing methods

Temperature profile: Zone 1: 140°С, Zone 2: 150°С, Zone 3: 170°С, Zone 4: 180°С, Die plate: 200°С.