PA METALENTA PA/EGF 50

Alternative and trade names
METALENTA PA/EGF 50
Want to keep this datasheet? Save it now in your required format

Description

METALENTA, a unidirectionally reinforced fiber glass tape, is a composite material based on a modified polymer, unidirectionally reinforced with glass roving and a complex of additives that give the material increased resistance to thermal oxidative degradation during processing and operation.

This material data has been provided by METACLAY .

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.65 g/cm³

Show Supplier Material materials with Density of 1.65 g/cm³

at 230°C

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

31 GPa

Show Supplier Material materials with Elastic modulus of 31 GPa

ISO 527-5/Tape, 1mm/min

Elongation

23.0 °C

2.5 %

Show Supplier Material materials with Elongation of 2.5 %

ISO 527-5/Tape, 5mm/min

Flexural modulus

23.0 °C

31 GPa

Show Supplier Material materials with Flexural modulus of 31 GPa

ISO 14125, 2mm/min

Flexural strength

23.0 °C

750 MPa

Show Supplier Material materials with Flexural strength of 750 MPa

ISO 14125, 2mm/min

Interlaminar shear strength

23.0 °C

23 MPa

Show Supplier Material materials with Interlaminar shear strength of 23 MPa

ISO 14130, 1mm/min

Tensile strength

23.0 °C

700 MPa

Show Supplier Material materials with Tensile strength of 700 MPa

ISO 527-5/Tape, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.3E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.3E-5 1/K

ISO 11359, 23-500°C at 50°C/min

Coefficient of thermal expansion, transverse

23.0 °C

1.2E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K

ISO 11359, 23-500°C at 50°C/min

Melting point

205 °C

Show Supplier Material materials with Melting point of 205 °C

ISO 11357, 100°C/min

Technological properties

Property
Application areas

METALENTA, a unidirectionally reinforced fiberglass tape, is applied for creation an external protective and reinforcing fiberglass coating of steel pipelines with a diameter 219 to 1420 mm with an external polymer anticorrosive coating. Fiberglass coating is designated to protect the anticorrosive polymer coating from mechanical stress during the construction, operation, repair and reconstruction of the pipeline. The material is also applied for creation an external protective layer of extrusion pipes and cables to prevent surface damage during installation and operation and for creation a reinforcing layer to strengthen the structure in the production of composite pipes, sheets, panels, honeycomb structures, etc.

Fillers

Glass Fiber