Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 15 GPa Show Supplier Material materials with Elastic modulus of 15 GPa | ISO 178 (Flexural Test) |
Elongation | 23.0 °C | 1.5 % Show Supplier Material materials with Elongation of 1.5 % | ISO 178 |
Flexural strength | 23.0 °C | 180 MPa Show Supplier Material materials with Flexural strength of 180 MPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 3 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 3 kJ/m² | ISO 179-1 |
Impact strength, Charpy unnotched | 23.0 °C | 16 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 16 kJ/m² | ISO 179-1 |
Tensile strength | 23.0 °C | 110 MPa Show Supplier Material materials with Tensile strength of 110 MPa | ISO 527 |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.4E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.4E-5 1/K | ISO 11359-2, Mean value for 20-105°C |
Glass transition temperature | 110 °C Show Supplier Material materials with Glass transition temperature of 110 °C | ISO 6721-7 | |
Thermal conductivity | 23.0 °C | 0.85 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.85 W/(m·K) | ISO 8894 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 250 V Show Supplier Material materials with Comparative tracking index of 250 V | IEC 60112 |
Dielectric constant, 50Hz | 23.0 °C | 4.7 [-] Show Supplier Material materials with Dielectric constant, 50Hz of 4.7 [-] | IEC 60250 |
Dielectric strength | 23.0 °C | 23 kV/mm Show Supplier Material materials with Dielectric strength of 23 kV/mm | IEC 60243-1, 3mm Plate |
Loss tangent, 50Hz | 23.0 °C | 1.3 [-] Show Supplier Material materials with Loss tangent, 50Hz of 1.3 [-] | IEC 60250 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 60093 |
Technological properties
Property | ||
---|---|---|
Application areas | Encapsulation of electrical devices e.g. Solenoids, Stators, Transformer | |
Fillers | Glass Fiber |